【摘要】：在紅外波長上轉(zhuǎn)換探測器氮化硅(SiN_x)鈍化層制作單層六角密排的二氧化硅(SiO_2)納米球陣列,以提高紅外波長上轉(zhuǎn)換探測器的整體效率.采用自組裝的方法在器件鈍化層上制備了直徑分別約為300,450,750和1000 nm的SiO_2納米球,并與無表面微納結(jié)構(gòu)器件進行對比測試.結(jié)果表明:鈍化層附著SiO_2納米球能有效地提高紅外波長上轉(zhuǎn)換器的光提取效率;當SiO_2納米球直徑為750 nm時的光提取效率最優(yōu),是無表面微納結(jié)構(gòu)器件的2.6倍,可實現(xiàn)低成本制作高效率紅外波長上轉(zhuǎn)換探測器.
[Abstract]:Fabrication of single-layer hexagonal SiO-2) nanospheres array with SiNX passivating layer of infrared wavelength up-conversion detector SiNX, In order to improve the overall efficiency of the infrared wavelength up-conversion detector, SiO_2 nanospheres with diameters of about 300450750 nm and 1000 nm were prepared on the passivated layer by self-assembly method. The results show that the passivation layer attached to the SiO_2 nanospheres can effectively improve the optical extraction efficiency of the infrared wavelength up-converter, and the optical extraction efficiency is optimal when the diameter of the SiO_2 nanospheres is 750nm. It is 2.6 times as high as the non-surface micro / nano structure device. It can be used to fabricate high efficiency infrared wavelength up-conversion detector at low cost.
【作者單位】： 長春理工大學光電工程學院;長春理工大學電子信息工程學院;
【基金】：國家自然科學基金(批準號:11474037,11474041)資助的課題~~
【分類號】：TN215
【相似文獻】
相關期刊論文 前3條
1 劉金庫,吳慶生,丁亞平,余意;銀、銅硫化物納米球的活性模板合成及其光學性能研究[J];功能材料;2004年06期
2 王兵;;香港大學利用熒光納米球讓LED發(fā)出白光[J];功能材料信息;2008年Z1期
3 鄧玉榮,丁曉夏,甘仲惟,高建明,程筠,賈志杰,黃新堂;化學氣相沉積法合成ZnS納米球[J];華中師范大學學報(自然科學版);2002年03期
相關碩士學位論文 前1條
1 桑士寶;中空二氧化鈦納米球的制備及其光催化性能研究[D];黑龍江大學;2013年
，本文編號：1684465
本文鏈接：http://sikaile.net/kejilunwen/dianzigongchenglunwen/1684465.html
教材專著