本文選題：Nd-Y-Fe-B快淬帶 + 快淬速度　； 參考：《鋼鐵研究總院》2017年碩士論文

【摘要】：隨著稀土資源的大量開(kāi)發(fā)和廣泛應(yīng)用,一方面Pr-Nd價(jià)格高,給企業(yè)帶來(lái)大的成本壓力;另一方面通過(guò)高成本分離提純出的大量Y、La、Ce被棄置浪費(fèi),造成環(huán)境污染與庫(kù)存飽和。開(kāi)發(fā)利用好高豐度、低價(jià)格的Y、La、Ce,無(wú)疑具有重要的經(jīng)濟(jì)和戰(zhàn)略意義。關(guān)于La和Ce替代的快淬帶已經(jīng)進(jìn)行了廣泛而系統(tǒng)的研究,到目前為止,還沒(méi)有系統(tǒng)的研究Y替代Nd對(duì)Nd-Fe-B快淬帶磁性和微結(jié)構(gòu)影響。本文系統(tǒng)制備了(Nd1-xYx)145FebalB6Co0.2Al1Cu0.15(x=0,0.1,0.2,0.3,0.4,0.5)六種快淬帶,研究了 Y替代Nd-Fe-B快淬帶制備的最佳工藝,系統(tǒng)研究了 Y替代Nd對(duì)Nd-Fe-B快淬帶磁性能、微結(jié)構(gòu)、矯頑力機(jī)制和晶粒間相互作用的影響。1、XRD、TMA、TEM結(jié)果表明快淬帶以2:14:1相為主,其中x=0.1,v=15 m/s快淬帶可以在晶界角隅處,觀察到第二相的聚集。隨著釔替代量的增加,晶粒尺寸增大。v=25 m/s快淬帶的晶粒尺寸從x=0時(shí)的18nm增加到x=0.4時(shí)的89.2 nm。2、隨著釔替代量的增加,(Nd1-xYx)14.5FebalB6(Co0.2Al1Cu0.15快淬帶的磁性能降低。在同一成分下,隨著快淬速度的增加,磁性能先升高后降低,在v = 25 m/s時(shí),獲得最佳磁性能,其中x=0-0.4時(shí),剩磁Br分別為8.01,7.83,7.71,7.66,7.09kGs;內(nèi)稟矯頑力 Hcj分別為 17.59,14.78,13.46,12.43,10.17kOe。x=0.3受到快淬速度的影響相對(duì)較小,當(dāng)快淬速度在15 m/s～30 m/s之間變化時(shí),快淬帶的磁性能和微觀結(jié)構(gòu)變化很小。隨著釔替代量的增加,快淬帶的居里溫度降低。3、通過(guò)初始磁化曲線和小回線研究了快淬帶的矯頑力機(jī)制。x=0的內(nèi)稟矯頑力 Hcj= 17.6kOe 在 Hsat=18.5kOe 時(shí)獲得;x=0.4 的內(nèi)稟矯頑力 Hcj= 10.17kOe在Hsat=12.5kOe時(shí)獲得,HcjHsat,因此快淬帶的矯頑力機(jī)制以釘扎型為主。初始磁化曲線表明隨著釔替代量的增加,形核作用加強(qiáng)。4、通過(guò)δM曲線分析得,磁化場(chǎng)較小時(shí),晶粒之間存在很強(qiáng)的交換耦合作用。x=0.1的δM峰值最小,只有0.586;x=0.4的δM曲線峰值為0.984,比沒(méi)有釔替代快淬帶的值都高。磁化場(chǎng)增大后,交換耦合作用降低,長(zhǎng)程靜磁耦合作用加強(qiáng)。
[Abstract]:With the extensive development and wide application of rare earth resources, on the one hand, Pr-Nd price is high, which brings great cost pressure to enterprises; on the other hand, a large number of YPL-LaCe purified by high cost separation are discarded and wasted, resulting in environmental pollution and inventory saturation. It is undoubtedly of great economic and strategic significance to develop and make use of the high abundance and low price Ya La-ce. The effects of Y substitution ND on the magnetic properties and microstructure of Nd-Fe-B quenched belts have been studied extensively and systematically. In this paper, Nd1-xYxC145FebalB6Co0.2Al1Cu0.15xOO0.1C 0.1C 0.2U 0.3U 0.4U) six kinds of quenched belts have been prepared systematically. The optimum process of preparing Y substitute for Nd-Fe-B quenched belts has been studied. The magnetic properties and microstructure of ND substituted ND on Nd-Fe-B quenched zones have been systematically studied. The effect of coercivity mechanism and grain interaction. The results of TMA-TEM show that the quenching band is mainly 2:14:1 phase, and the second phase aggregation can be observed at the corner of grain boundary. With the increase of yttrium substitution, the grain size of the quenched strip increases from 18nm at x = 0 to 89.2 nm.2at x = 0.4.The magnetic properties of the quenched strip decrease with the increase of the substitution amount of yttrium, Nd1-xYxX 14.5 FebalB6Co0.2Al1Cu0.15. In the same composition, with the increase of the quenching speed, the magnetic properties first increase and then decrease, and the optimum magnetic properties are obtained at v = 25 m / s, where x = 0. 4, The remanent magnetic flux (Br) is 8.01 ~ 7.83n 7.83n 7.61G / s, and the intrinsic coercivity HCJ is 17.59U 14.78C 13.46C 12.43n 10.17kOe.x0.3 respectively. The magnetic properties and microstructure of the quenched zone are very small when the quenching rate varies from 15 m/s~30 m / s to 10.17kOe.x0.3.The results show that the magnetic properties and microstructure of the quenched zone are very small when the quenching rate varies between 15 m/s~30 m / s and 10.17 kOe.x0.The magnetic properties and microstructure of the quenched zone are very small. With the increase of yttrium substitution, The Curie temperature of the quenched band is decreased by .3.The coercivity mechanism of the quenched tape is studied by the initial magnetization curve and the small loop. The intrinsic coercivity HCJ = 17.6 KOe obtained at Hsat-18.5kOe is the intrinsic coercivity HCJ = 10.17kOe at Hsat12.5kOe, so the intrinsic coercivity HCJ = 10.17kOe is obtained at Hsat-12.5kOe, so the intrinsic coercivity HCJ = 10.17kOe is obtained at Hsat-12.5kOe, so the intrinsic coercivity HCJ = 10.17kOe is obtained. The coercivity mechanism of quenched band is mainly pinning type. The initial magnetization curve shows that with the increase of the substitution amount of yttrium, nucleation is strengthened .4.The 未 M peak value with strong exchange coupling between the grains is minimum when the magnetization field is small. The peak value of 未 M curve is 0.984, which is higher than that without yttrium instead of quenched band. When the magnetization field increases, the exchange coupling decreases and the long-term magnetostatic coupling becomes stronger.
【學(xué)位授予單位】：鋼鐵研究總院
【學(xué)位級(jí)別】：碩士
【學(xué)位授予年份】：2017
【分類號(hào)】：TM273

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 王新林;我國(guó)快淬金屬產(chǎn)業(yè)的形成與發(fā)展[J];物理;1993年05期

2 吳安國(guó);快淬;熔體快淬,熔體旋淬,熔淬[J];磁性材料及器件;2000年01期

3 王永強(qiáng);李兆波;李世貴;;兩種納米晶釹鐵硼快淬條帶制備技術(shù)比較[J];磁性材料及器件;2008年01期

4 王永強(qiáng);李兆波;李世貴;彭方元;;國(guó)內(nèi)快淬釹鐵硼磁粉生產(chǎn)技術(shù)及其裝備的發(fā)展——電弧重熔溢流快淬與晶化工藝的改進(jìn)[J];磁性材料及器件;2007年06期

5 郭萬(wàn)林;李天文;淮軍鋒;;FeSiB纖維的快淬制備及其性能[J];航空材料學(xué)報(bào);2006年03期

6 羅廣圣,羅根香,閻阿儒;快淬磁各向異性SmCo_5的結(jié)構(gòu)和磁性[J];稀土;2002年01期

7 包小倩,張茂才,喬垎,高學(xué)緒,劉湘華,周壽增;快淬Sm-Fe-Cu-Si-C合金帶的組織與磁性能[J];磁性材料及器件;2002年02期

8 王晨;嚴(yán)密;;快淬設(shè)備對(duì)Nd_2Fe_(14)B/α-Fe合金微結(jié)構(gòu)和磁性能的影響[J];中國(guó)稀土學(xué)報(bào);2008年04期

9 張敏剛,郭東城,孔海旺,金志浩;快淬NdFeB永磁合金的晶化行為[J];太原重型機(jī)械學(xué)院學(xué)報(bào);1999年03期

10 徐孝榮,姚國(guó)蘭,崔貴根,林崇業(yè),傅慶科;快淬Nd-Fe-Co-Zr-B合金磁性研究[J];磁性材料及器件;2001年04期

相關(guān)會(huì)議論文 前10條

1 黃照華;周邦新;楊仕清;;單輥熔體快淬凝固工藝的數(shù)學(xué)物理分析[A];2006全國(guó)核材料學(xué)術(shù)交流會(huì)論文集[C];2006年

2 王新林;張羊換;趙棟梁;;真空快淬材料研究的新近進(jìn)展[A];第五屆中國(guó)功能材料及其應(yīng)用學(xué)術(shù)會(huì)議論文集Ⅰ[C];2004年

3 郭萬(wàn)林;李天文;淮軍鋒;;FeSiB纖維的快淬制備及其性能[A];第四屆數(shù)控機(jī)床與自動(dòng)化技術(shù)高層論壇論文集[C];2013年

4 孫鋼;張敏剛;柴躍生;;Nd-Fe-B雙相復(fù)合永磁合金快淬帶織構(gòu)與顯微分析[A];第二屆全國(guó)掃描電子顯微學(xué)會(huì)議論文集[C];2001年

5 許用華;孫愛(ài)芝;李琪;蘇廣春;肖耀福;;Nd_2Fe_(14)B/α-Fe雙相快淬粉晶化行為研究[A];2004年材料科學(xué)與工程新進(jìn)展[C];2004年

6 許用華;孫愛(ài)芝;李琪;蘇廣春;肖耀福;;Nd_2Fe_(14)B/α-Fe雙相快淬粉晶化行為研究[A];2004中國(guó)稀土永磁材料論壇論文集[C];2004年

7 許用華;孫愛(ài)芝;李琪;蘇廣春;肖耀福;;Nd_2Fe_(14)B/α-Fe雙相快淬粉晶化行為研究[A];2004年中國(guó)材料研討會(huì)論文摘要集[C];2004年

8 劉琦;孫占波;;熔體快淬CuCr觸頭材料的制備與性能[A];2008全國(guó)功能材料科技與產(chǎn)業(yè)高層論壇論文集[C];2008年

9 劉榮明;那冉;鄧韻文;劉衛(wèi)強(qiáng);岳明;張久興;;高矯頑力Tb-Fe-B快淬薄帶的結(jié)構(gòu)與磁性能研究[A];第七屆中國(guó)功能材料及其應(yīng)用學(xué)術(shù)會(huì)議論文集（第3分冊(cè)）[C];2010年

10 周壽增;王佐誠(chéng);張茂才;高學(xué)緒;喬偉;;快淬速度對(duì)Pr_8Fe_(86)B_6合金快淬帶組織結(jié)構(gòu)與性能的影響[A];第四屆中國(guó)功能材料及其應(yīng)用學(xué)術(shù)會(huì)議論文集[C];2001年

相關(guān)重要報(bào)紙文章 前2條

1 ;真空復(fù)合熔煉快淬爐[N];中國(guó)有色金屬報(bào);2003年

2 記者　 徐朝暉 實(shí)習(xí)生 曹川;“朝日科”叫板磁業(yè)跨國(guó)公司[N];金華日?qǐng)?bào);2006年

相關(guān)碩士學(xué)位論文 前10條

1 白帆;熱壓(Nd,Ce)FeB/CaF_2復(fù)合磁體的磁電性能和微結(jié)構(gòu)研究[D];河北工程大學(xué);2016年

2 韓寧;C摻雜對(duì)La-Fe-Si合金快淬條帶磁熱性能的影響[D];上海工程技術(shù)大學(xué);2016年

3 鄭蒙;釹釔鐵硼快淬帶的磁性與微結(jié)構(gòu)[D];鋼鐵研究總院;2017年

4 裴坤;高豐度稀土元素對(duì)快淬Nd-Fe-B磁粉性能和結(jié)構(gòu)的影響[D];中北大學(xué);2016年

5 毛昌森;快淬NdFeB磁粉及其粘結(jié)磁體磁性能的研究[D];浙江大學(xué);2005年

6 段瓔W，

本文編號(hào)：2047505