【摘要】：為研究納米ZnO摻雜對(duì)環(huán)氧樹脂復(fù)合材料絕緣特性的影響,以納米ZnO改性雙酚A型環(huán)氧樹脂材料為研究對(duì)象,考察了不同摻雜量下復(fù)合材料直流電導(dǎo)、介電常數(shù)等絕緣特征參數(shù)的變化趨勢(shì);并利用針板電極系統(tǒng),分別對(duì)ZnO/環(huán)氧和SiO_2/環(huán)氧復(fù)合材料進(jìn)行了起始局放電壓對(duì)比測(cè)試。研究發(fā)現(xiàn),當(dāng)納米ZnO質(zhì)量分?jǐn)?shù)15%時(shí),復(fù)合材料開始呈現(xiàn)非線性電導(dǎo)特性,復(fù)合材料介電常數(shù)也發(fā)生顯著變化,質(zhì)量分?jǐn)?shù)為30%時(shí)其電導(dǎo)非線性系數(shù)可達(dá)到18.7,介電常數(shù)則可上升至5.9。相同電極結(jié)構(gòu)下,納米ZnO/環(huán)氧復(fù)合材料的起始局放電壓顯著高于SiO_2/環(huán)氧復(fù)合材料,ZnO質(zhì)量分?jǐn)?shù)為15%時(shí)起始局放起始電壓達(dá)到最大值,分別比無摻雜樹脂及納米SiO_2摻雜樹脂提高了33%和22%。研究表明,納米ZnO粒子的引入顯著提高了環(huán)氧樹脂復(fù)合材料的絕緣性能,納米ZnO粒子的界面效應(yīng)和非線性電導(dǎo)特性在改善復(fù)合樹脂絕緣特性方面發(fā)揮了主要作用。
[Abstract]:In order to study the effect of nano ZnO doping on the insulating properties of epoxy resin composites, the direct current conductance of composites with different doping amounts was investigated by using nano ZnO modified bisphenol A epoxy resin as the research object. The variation trend of dielectric constant and other insulation characteristic parameters, and the comparison of initial partial discharge voltage between ZnO/ epoxy and SiO_2/ epoxy composites were carried out by using the needle plate electrode system. It is found that when the mass fraction of nanometer ZnO is 15, the composite begins to exhibit nonlinear conductivity, and the dielectric constant of the composite also changes significantly. When the mass fraction is 30, the nonlinear coefficient of conductivity can reach 18.7, and the dielectric constant can rise to 5.9. At the same electrode structure, the initial partial discharge voltage of nano-sized ZnO/ epoxy composites is significantly higher than that of SiO_2/ epoxy composites with a mass fraction of 15. Compared with the non-doped resin and the nano-SiO_2 doped resin, it increased by 33% and 22%, respectively. The results show that the introduction of nanometer ZnO particles can significantly improve the insulating properties of epoxy resin composites, and the interfacial effect and nonlinear conductivity of nano ZnO particles play a major role in improving the insulating properties of composite resins.
【作者單位】： 西安理工大學(xué)電力工程系;安徽理工大學(xué)電氣與信息工程學(xué)院;
【基金】：國家自然科學(xué)基金(51607003;51279161) 西北旱區(qū)生態(tài)水利工程國家重點(diǎn)實(shí)驗(yàn)室基金(2016ZZKT-12) 陜西省教育廳科研計(jì)劃項(xiàng)目基金(16JK1562)~~
【分類號(hào)】：TM215.1

【相似文獻(xiàn)】

相關(guān)期刊論文 前4條

1 高翠芹;安從俊;程建平;;納米氧化鋅的制備和電化學(xué)性能研究[J];電池工業(yè);2006年01期

2 陳少卿;張宏亮;成霞;;納米氧化鋅/低密度聚乙烯抗光老化性能的熱刺激電流分析[J];絕緣材料;2008年01期

3 陳其猛;易雙萍;趙渺;;納米氧化鋅對(duì)鎳氫電池電化學(xué)性能的影響[J];稀有金屬材料與工程;2010年S1期

4 陳少卿;成霞;王霞;屠德民;;納米氧化鋅/聚乙烯復(fù)合材料中空間電荷及體積電阻率的研究[J];絕緣材料;2007年02期

相關(guān)碩士學(xué)位論文 前3條

1 董一帆;納米氧化鋅的制備和在有機(jī)太陽能電池的應(yīng)用[D];華南理工大學(xué);2016年

2 余熙;納米氧化鋅粉的控制制備及染料敏化太陽能電池的研究[D];景德鎮(zhèn)陶瓷學(xué)院;2010年

3 龔贏贏;超級(jí)電容器用納米氧化鋅/石墨烯復(fù)合材料的制備與應(yīng)用研究[D];成都理工大學(xué);2014年

，

本文編號(hào)：1826071