本文選題：鋰離子電池　切入點：共沉淀　出處：《硅酸鹽學報》2017年07期 　論文類型：期刊論文

【摘要】：以乙酸鎳、乙酸錳為原料,碳酸氫鈉為沉淀劑,利用共沉淀法制備了鎳錳碳酸鹽前驅(qū)體,并在還原氣氛中通過控制還原法制備了具有不同Mn/Ni摩爾比的球形MnO@Ni負極材料,并對其成分、形貌和元素分布及電化學性能進行表征。結果表明:通過在MnO體相中均勻摻入合適比例的高導電性金屬鎳,可以有效提高鋰離子電池負極材料MnO的電化學性能。Mn/Ni摩爾比為1:10時,MnO@Ni負極材料5C放電比容量為214.3 mA·h/g,0.5C循環(huán)200次容量保持率為72%,呈現(xiàn)出高的倍率性能和循環(huán)保持率。
[Abstract]:Using nickel acetate and manganese acetate as raw materials and sodium bicarbonate as precipitant, the nickel-manganese carbonate precursor was prepared by co-precipitation method. The spherical MnO@Ni anode material with different Mn/Ni molar ratio was prepared by controlled reduction in reducing atmosphere. The composition, morphology, element distribution and electrochemical properties were characterized. The results showed that the proper proportion of high conductivity nickel was added into the bulk phase of MnO. When the molar ratio of mn / Ni is 1:10, the discharge specific capacity of 5C anode material is 214.3 Ma 路g / g ~ (0.5) C cycle, and the capacity retention rate is 72%, showing a high rate of performance and a high cycle retention rate, which can effectively improve the electrochemical performance of the cathode material of Li-ion battery with the molar ratio of mn / Ni at 1:10, and the discharge specific capacity of 5C is 214.3 Ma / g / g ~ (0.5) C cycle.
【作者單位】： 合肥工業(yè)大學化學與化工學院;
【基金】：國家自然科學基金項目(21271058,91534102) 安徽省科技攻關項目(1501021013)
【分類號】：TM912

【參考文獻】

相關期刊論文 前1條

1 劉雅敏;趙秀蕓;夏定國;;微/納米結構MnO負極材料的制備與儲鋰性能[J];電源技術;2012年05期

相關碩士學位論文 前1條

1 馮玉龍;中空球形錳基鋰離子電池負極材料的制備及其儲鋰性能研究[D];北京化工大學;2014年

【共引文獻】

相關期刊論文 前4條

1 孫永輝;高強;范小明;田院;楊則恒;張衛(wèi)新;;控制還原法制備高性能MnO@Ni鋰離子電池負極材料[J];硅酸鹽學報;2017年07期

2 孟芬芬;郭志巖;;水熱法制備SiO_2@Mn_2O_3球形納米粒子[J];青島科技大學學報(自然科學版);2016年04期

3 王帆;傅小明;;制備MnO納米顆粒的新方法[J];科技通報;2015年01期

4 殷木一;丁朋;張凌;李偉;;Ag包覆MnO鋰離子電池負極材料的合成及性能[J];化工新型材料;2013年07期

【二級參考文獻】

相關期刊論文 前1條

1 柏大偉;何雨石;陽炳檢;廖小珍;馬紫峰;;石墨烯納米片-氧化亞鈷負極材料制備與表征[J];電源技術;2011年02期

，

本文編號：1649251