本文選題：換流變壓器　切入點：油紙絕緣　出處：《高電壓技術》2017年09期 　論文類型：期刊論文

【摘要】：為研究陷阱參數(shù)對納米蒙脫土(MMT)改性絕緣紙板介電特性的影響,探索出實驗室制備納米MMT改性絕緣紙板工藝。研究了其力學性能及介電特性隨納米摻雜比例的變化規(guī)律,借助熱刺激電流(TSC)法測量了不同摻雜比例下改性紙板的陷阱參數(shù),分析了納米摻雜對改性紙板力學性能及介電特性的影響機理。試驗結(jié)果表明:隨著MMT納米摻雜比例的提高,改性絕緣紙板的介電常數(shù)和機械抗張強度呈現(xiàn)先降低后升高的趨勢。納米MMT的摻雜使紙板電導率增加,其非線性拐點對應電場強度隨納米摻雜比例的提高逐漸降低。擊穿場強隨納米摻雜比例的增加呈先增后降趨勢。借助能帶理論分析得出,陷阱電荷量的增加將導致改性紙板的非線性電導率上升;陷阱深度的增加將提高改性紙板擊穿場強,陷阱特性是影響改性紙板介電特性變化的主要原因。
[Abstract]:In order to study the effect of trap parameters on the dielectric properties of nano-montmorillonite modified insulating paperboard, the preparation process of nano-MMT modified insulating paperboard in laboratory was explored. The variation of mechanical properties and dielectric properties with nano-doping ratio was studied. The trap parameters of modified paperboard with different doping ratios were measured by means of thermal stimulated current (TSC) method, and the influence mechanism of nano-doping on the mechanical properties and dielectric properties of modified paperboard was analyzed. The experimental results showed that: with the increase of nano-doping ratio of MMT, the effect of nano-doping on the mechanical properties and dielectric properties of modified paperboard was analyzed. The dielectric constant and mechanical tensile strength of modified insulating paperboard decreased first and then increased. The corresponding electric field intensity at the nonlinear inflection point decreases with the increase of nano-doping ratio, and the breakdown field strength increases first and then decreases with the increase of nano-doping ratio. The increase of trap charge will lead to the increase of nonlinear conductivity of modified paperboard, and the increase of trap depth will increase the breakdown field strength of modified paperboard, and the trap property is the main reason that affects the change of dielectric properties of modified paperboard.
【作者單位】： 哈爾濱理工大學工程電介質(zhì)及其應用教育部重點實驗室;國網(wǎng)黑龍江省電力有限公司電力科學研究院;
【基金】：國家自然科學基金(51407051;51677046) 黑龍江省普通本科高等學校青年創(chuàng)新人才培養(yǎng)計劃(編號略)~~
【分類號】：TM215.6

【相似文獻】

相關期刊論文 前5條

1 葉建鑄;楊嘉祥;王新掌;黃程偉;;含水量對石蠟介電特性的影響[J];電工材料;2009年03期

2 周健,劉桂珍,潘勁,程吉平,梅炳初;Al_2O_3 陶瓷的微波介電特性研究[J];武漢交通科技大學學報;1999年04期

3 尹桂來;李建英;成鵬飛;李盛濤;;Ag/ZnO復合體系的介電特性研究[J];稀有金屬材料與工程;2008年08期

4 卓蓉暉,孟范成,張輝,方亮;鉭酸鹽Ba_5LaZnTa_9O_(30)的結(jié)構(gòu)及其介電特性[J];武漢理工大學學報;2004年04期

5 史云;侯育冬;葛海燕;朱滿康;嚴輝;;TiO_2晶型對FeTiTaO_6陶瓷介電特性的影響[J];稀有金屬材料與工程;2011年S1期

相關會議論文 前1條

1 王改花;代波;馬擁軍;任勇;;碳纖維的微波介電性能研究[A];2012中國功能新材料學術論壇暨第三屆全國電磁材料及器件學術會議論文摘要集[C];2012年

相關博士學位論文 前1條

1 席新明;基于介電特性的流體組分檢測方法與技術研究[D];西北農(nóng)林科技大學;2012年

，

本文編號：1611622