【摘要】：通過在空氣和氮氣中不同溫度的退火處理對氧化鋅內部缺陷進行調控,并研究了缺陷調控對氧化鋅光電響應和恢復性能的影響。在空氣氣氛中,隨著退火溫度的升高,氧空位和鋅空位的濃度逐漸增加。在氮氣中高溫退火后,氧空位濃度增加,鋅空位卻被湮滅。退火后的氧化鋅納米棒陣列比未退火的氧化鋅納米棒陣列表現(xiàn)出更顯著的光電恢復效率(最高提高約40倍),然而,退火后的氧化鋅納米棒陣列對紫外光的光電響應速率卻被減弱。
[Abstract]:The internal defects of zinc oxide were regulated by annealing at different temperatures in air and nitrogen, and the effects of defects on the photoelectric response and recovery performance of zinc oxide were studied. With the increase of annealing temperature, the concentration of oxygen vacancy and zinc vacancy increase in air atmosphere. After high temperature annealing in nitrogen, the oxygen vacancy concentration increases, but the zinc vacancy is annihilated. The annealed ZnO nanorods showed a more significant photoelectric recovery efficiency than unannealed ZnO nanorods (up to 40 times higher), however, The photoresponse rate of annealed ZnO nanorods to ultraviolet light is weakened.
【作者單位】： 華中科技大學材料科學與工程學院;
【基金】：國家自然科學基金資助項目(50927201)
【分類號】：O614.241;TB383.1

【相似文獻】

相關期刊論文 前9條

1 于威;朱海榮;趙一;孫宇凱;盧海江;傅廣生;;初始晶硅多層薄膜光電響應及載流子輸運特性[J];科學通報;2013年04期

2 王敖金,鄭國和,胡坤生,吳海民,陸祖宏;電沉積紫膜薄膜中菌紫質的光電響應對N-端表面的金屬陽離子濃度的依賴性[J];感光科學與光化學;1997年03期

3 周國定,ModestovAD,潘傳智,楊邁之,蔡生民;銅電極光電響應p型轉變?yōu)閚型的機理探討[J];物理化學學報;1995年01期

4 梅燕,賈振斌,曹江林,韓梅娟,張艷峰,魏雨;納米TiO_2粉體的固定及其對甲醇的光電復合氧化[J];太陽能學報;2002年02期

5 張潔;陳俞霖;;有序碳納米管的光電響應實驗[J];光電子.激光;2012年03期

6 康志敏,郝彥忠,孫寶,王慶飛,童汝亭;制備工藝對TiO_2納米結構電極光電響應的影響[J];河北科技大學學報;2004年02期

7 鄧杰;陶杰;高潔;秦琦;;聚苯胺/TiO_2復合納米膜電極的制備及其光電性能[J];功能材料;2012年07期

8 康志敏,郝彥忠,王慶飛,童汝亭,李軍鎖;煅燒溫度對納米TiO_2光電響應的影響[J];化學研究與應用;2004年02期

9 ;[J];;年期

相關會議論文 前1條

1 楊儉華;;菌紫質膜光電響應系統(tǒng)電勢源的多源性探討[A];第五屆全國光生物學學術討論會論文摘要集[C];2000年

相關碩士學位論文 前6條

1 趙祺e，

本文編號：2361231