【摘要】：采用納米金屬結(jié)合劑PcBN復(fù)合片制備技術(shù),在六面頂壓機(jī)上合成出直徑為Φ55mm的PcBN復(fù)合片。經(jīng)性能測(cè)試,磨耗比5425,維氏硬度5980HV,cBN層抗彎強(qiáng)度516.6MPa,經(jīng)超聲波微成像分析,樣品無分層、裂紋、夾雜、cBN厚度不均等缺陷,制成刀具后,在切削軸承鋼Gr15時(shí),樣品與國(guó)外同類產(chǎn)品性能相當(dāng)。
[Abstract]:The PcBN composite sheet with diameter 桅 55mm was synthesized on a six-sided top press by using the preparation technology of nano-metal binder PcBN composite sheet. The wear ratio 5425, Vickers hardness 5980HVN CBN layer bending strength 516.6MPa, the samples without delamination, crack, inclusions and CBN thickness inhomogeneity defects were obtained by ultrasonic microimaging analysis. The cutting tool was made when cutting bearing steel Gr15. The properties of the samples are comparable to those of similar products abroad.
【作者單位】： 中南鉆石有限公司;
【基金】：河南省2011年扶持企業(yè)自主創(chuàng)新資金項(xiàng)目(合同編號(hào):ZNZSKY201101-1)
【分類號(hào)】：TB33

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 馬成龍;;金剛石復(fù)合片沖擊抗力的測(cè)定[J];鑿巖機(jī)械氣動(dòng)工具;2009年03期

2 楊威,趙大鋼,汪玉樹;金剛石復(fù)合片主要缺陷及產(chǎn)生的原因討論[J];金剛石與磨料磨具工程;2001年03期

3 司效東;金剛石復(fù)合片燒結(jié)體磨耗比的提高[J];大慶石油學(xué)院學(xué)報(bào);2004年01期

4 周建強(qiáng),艾興,李兆前,鄧建新;陶瓷/硬質(zhì)合金復(fù)合片殘余應(yīng)力分析[J];應(yīng)用力學(xué)學(xué)報(bào);1999年03期

5 李穎 ,韓秀麗 ,王孝琪;金剛石復(fù)合片機(jī)械性能的研究[J];金剛石與磨料磨具工程;2001年05期

6 賈志宏,王貴成;梯度復(fù)合片的組織與耐熱性[J];農(nóng)業(yè)機(jī)械學(xué)報(bào);2005年06期

7 王適,張弘_";PCD復(fù)合片熱穩(wěn)定性的灰色關(guān)聯(lián)分析[J];機(jī)械科學(xué)與技術(shù);2003年S2期

8 黎明發(fā);張力;吳永橋;孫振亞;范端;田旭;葉先賢;;金剛石復(fù)合片的性能檢測(cè)及發(fā)展趨勢(shì)[J];武漢理工大學(xué)學(xué)報(bào)(信息與管理工程版);2007年06期

9 ;成果轉(zhuǎn)化[J];中國(guó)軍轉(zhuǎn)民;2001年12期

10 ;[J];;年期

相關(guān)會(huì)議論文 前1條

1 李端心;黎明發(fā);張力;;聚晶金剛石復(fù)合片顯微結(jié)構(gòu)的SEM研究[A];全國(guó)首屆青年復(fù)合材料學(xué)術(shù)交流會(huì)論文集[C];2007年

相關(guān)碩士學(xué)位論文 前3條

1 鄭安;國(guó)內(nèi)外復(fù)合片成分組織差異分析及機(jī)理研究[D];武漢理工大學(xué);2004年

2 趙京;金剛石復(fù)合片溫度場(chǎng)可視化測(cè)量研究[D];武漢理工大學(xué);2007年

3 李丹;不同粘結(jié)劑PcBN復(fù)合片的研究[D];四川大學(xué);2007年

，

本文編號(hào)：2259060