【摘要】：為探討聚脲金屬復合結構在低速沖擊下的動態(tài)響應,基于霍普金森桿發(fā)射系統(tǒng)驅動圓柱形子彈對聚脲和鋁板組成的方形板件,進行了10~17 m/s的低速沖擊試驗,其中試件包括單一鋁板、涂層結構和三明治結構3種配置,并保持了相同的面密度(1.49 g/cm2)。從受沖擊面破壞形貌、剩余變形和變形時程等方面對試驗結果進行了分析。結果表明,聚脲層涂覆在受沖擊側可以有效緩解有棱沖擊體帶來的應力集中現(xiàn)象,具有相同面密度的純鋁板結構比背面涂層結構和夾層結構具有更強的抗局部剪切能力和抵抗變形能力。
[Abstract]:In order to investigate the dynamic response of polyurea metal composite structure under low speed impact, a low speed impact test of 10 ~ (17) m / s was carried out on a square plate composed of polyurea and aluminum plate driven by a cylindrical bullet driven by a Hopkinson rod launcher system. The specimen consists of a single aluminum plate, a coating structure and a sandwich structure with the same surface density (1. 49 g/cm2). The experimental results are analyzed from the aspects of the failure morphology, residual deformation and deformation time history of the impact surface. The results show that the polyurea coating on the impacted side can effectively alleviate the stress concentration caused by the impact body with edges. The pure aluminum plate structure with the same surface density has stronger local shear resistance and deformation resistance than the back coating structure and sandwich structure.
【作者單位】： 北京理工大學爆炸科學與技術國家重點實驗室;
【分類號】：TB333

【相似文獻】

相關期刊論文 前4條

1 黃微波;陳國華;盧敏;張效慈;;聚脲柔性減阻材料的制備及性能[J];高分子材料科學與工程;2007年03期

2 鐘萍;廖有為;肖鑫;彭恩高;李健;;聚脲涂層在兩種不同摩擦條件下的磨損行為探討[J];潤滑與密封;2008年09期

3 楊保平;席滿意;崔錦峰;郭軍紅;崔卓;;乙二醇改性聚脲微膠囊相變材料的研制[J];應用化工;2014年01期

4 張未來;;各類管道耐磨材料分析及納米復合聚脲耐磨防腐涂層[J];上海涂料;2009年05期

相關會議論文 前2條

1 林英民;;XW料界“奇葩”——\ 臺pc聚脲/奈米}聚脲之m鷫媅A];2010年海峽兩岸功能性復合材料論壇論文集[C];2010年

2 林英民;;奈米}聚脲[A];2010年海峽兩岸功能性復合材料論壇論文集[C];2010年

相關重要報紙文章 前1條

1 駱林　宋世琦;聚脲研討會暨秀珀洽談會成功舉行[N];建筑時報;2009年

相關碩士學位論文 前3條

1 韓曉倩;聚酰亞胺-b-聚脲共聚物薄膜的制備研究[D];大連理工大學;2016年

2 吳沖;玻璃纖維/聚脲復合材料的微觀結構與力學性能研究[D];哈爾濱工業(yè)大學;2013年

3 邸春陽;噴涂型聚氨酯/聚脲耐磨材料的制備及性能研究[D];哈爾濱工程大學;2012年

，

本文編號：2251902