發(fā)布時間：2018-09-11 12:18

【摘要】：基于薄膜表面裝飾工藝原理及DSGZ黏彈性本構模型的ABAQUS用戶材料子程序,對鼠標外殼貼膜的工藝過程進行仿真分析。分析結果表明,薄膜的厚度最厚為0.200 4 mm,最薄為0.182 1 mm,在X方向上的最大變形量為8.01 mm,在Y方向上的最大變形量為2.939 mm。然后對模外裝飾貼膜工藝參數(shù)進行DOE分析,分析結果表明,模腔的真空度、常壓加壓時間、高壓加壓時間對其厚度的標準偏差具有較大的正效應,高壓加壓時間對其在X、Y方向變形量的標準偏差也具有很大的正效應。
[Abstract]:Based on the principle of membrane surface decoration and the ABAQUS user material subroutine of DSGZ viscoelastic constitutive model, the process of mouse shell coating was simulated and analyzed. The results show that the thickness of the film is 0.200 4 mm, the thinnest is 0.182 1 mm, the maximum deformation in X direction is 8.01 mm, and the maximum deformation in Y direction is 2.939 mm.. Then, the DOE analysis of the process parameters of the decorative film is carried out. The results show that the vacuum degree of the cavity, the pressure time at normal pressure, and the pressure time at high pressure have a great positive effect on the standard deviation of the thickness of the film. High pressure time also has a great positive effect on the standard deviation of the deformation in the XY direction.
【作者單位】： 華東交通大學交通運輸與物流學院;華東交通大學機電與車輛工程學院;
【分類號】：TB306

【相似文獻】

相關期刊論文 前10條

1 湯華娟;;科技生產(chǎn)人員的良師益友 工藝設備技術的發(fā)展創(chuàng)新——介紹王承遇、陶瑛、谷秀梅編著《玻璃表面裝飾(第2版)》[J];玻璃與搪瓷;2010年06期

2 王承遇;姜妍彥;盧琪;龐世紅;陶瑛;;我國玻璃表面裝飾的現(xiàn)狀及發(fā)展方向[J];玻璃與搪瓷;2011年01期

3 小池弘之;童連祥;;表面裝飾紋設計[J];模具技術;1988年04期

4 劉先曙;鈦應用三則[J];稀有金屬材料與工程;1990年06期

5 岳新元;糕點表面裝飾法[J];烹調(diào)知識;1998年01期

6 高大彬;銅表面裝飾著色新工藝[J];表面技術;1994年03期

7 王承遇，陶瑛;玻璃表面裝飾技術（四）[J];玻璃與搪瓷;1996年02期

8 趙子夫 ,唐利;漢代家具的文化特征 二、動與緊[J];家具與環(huán)境;1994年01期

9 ;塑料制品表面裝飾技術的發(fā)展趨勢[J];化工文摘;2001年03期

10 官冬玲;;簡析木質(zhì)材料表面裝飾的綠色化[J];才智;2010年35期

相關會議論文 前2條

1 王承遇;姜妍彥;盧琪;龐世紅;陶瑛;;我國玻璃表面裝飾的現(xiàn)狀及發(fā)展方向[A];2010全國玻璃技術交流研討會論文集[C];2010年

2 唐丁寧;;表面裝飾工藝研究的現(xiàn)狀和展望[A];中國電子學會生產(chǎn)技術學會計算機數(shù)控技術研討會論文集[C];1990年

相關博士學位論文 前1條

1 蘇潤洲;木質(zhì)材料表面裝飾用材的光致變色機理的研究[D];東北林業(yè)大學;2011年

相關碩士學位論文 前1條

1 姚杰;薄膜表面裝飾模外成型裝備研究[D];浙江工業(yè)大學;2015年

，

本文編號：2236667