【摘要】：金屬有機骨架(MOFs)是一類新型的多孔納米材料,由金屬團簇和有機配體自組裝而成。由于具有超高的表面積、可控的孔尺寸和可調的化學環(huán)境等優(yōu)點,使其在空氣凈化、化學傳感、氣體存儲、催化和CO2捕捉等方面表現出非常好的應用前景。然而水穩(wěn)定性一直是阻礙其工業(yè)化應用的瓶頸,所以研究MOFs和水的相互作用及MOFs的水解機理具有非常重要的意義。主要從MOFs水穩(wěn)定性的研究方法,影響因素,如何增強MOFs的抗水性和有關MOFs水穩(wěn)定性研究的最新動態(tài)等方面進行了詳細論述,并指出了當前存在的問題和今后的發(fā)展方向。
[Abstract]:Organometallic skeleton (MOFs) is a new kind of porous nanomaterials, which is composed of metal clusters and organic ligands. Due to its high surface area, controllable pore size and adjustable chemical environment, it has a promising future in air purification, chemical sensing, gas storage, catalysis and CO2 capture. However, water stability has been the bottleneck of its industrial application, so it is of great significance to study the interaction between MOFs and water and the hydrolysis mechanism of MOFs. In this paper, the research methods, influencing factors, how to enhance the water resistance of MOFs and the latest trends in the study of water stability of MOFs are discussed in detail, and the existing problems and the future development are pointed out.
【作者單位】： 河南工業(yè)大學理學院;
【基金】：國家自然科學基金(11304079、11404094、11504088) 國家留學基金(201508410255) 河南省高等學校青年骨干教師(HNQG001316) 河南省省屬高校基本科研業(yè)務費專項資金資助的課題(2014YWQQ21)
【分類號】：TB383.1

【相似文獻】

相關博士學位論文 前2條

1 宗恩敏;鋯化炭基復合材料的合成及其對磷酸鹽的吸附性能研究[D];南京大學;2013年

2 孫西同;磁性高分子復合材料的制備及對Cr(Ⅵ)的吸附性能研究[D];中國科學院研究生院(過程工程研究所);2015年

相關碩士學位論文 前10條

1 苗晉朋;Cu-BTC@GO復合材料的機械化學合成與成型及其吸附性能研究[D];華南理工大學;2015年

2 李偉平;偕胺肟基—聚丙烯腈/剝離鈉基蒙脫石復合材料的合成及對鈾的吸附性能研究[D];蘭州大學;2015年

3 邢海濤;基于石墨烯復合材料的制備及其對重金屬離子的吸附性能研究[D];閩南師范大學;2015年

4 姚蔓莉;介孔氧化硅和介孔炭基納米材料的制備及其二氧化碳吸附性能研究[D];浙江師范大學;2015年

5 孔童童;氨基功能化多孔材料的制備及其CO_2吸附性能研究[D];青島科技大學;2016年

6 邢靜;系列納米過渡金屬氧化物的制備及其吸附性能研究[D];青島科技大學;2016年

7 黃虹;二硒化鉬及其復合材料的制備和吸附性能研究[D];江蘇大學;2016年

8 方貝貝;金屬氧化物復合材料的制備及其對有機染料的吸附性能研究[D];吉林大學;2016年

9 王瑋;功能納米復合材料的設計制備及吸附性能研究[D];燕山大學;2016年

10 張旭陽;Cu-MOF/PLA熔噴用復合材料的制備及重金屬吸附性能研究[D];浙江理工大學;2017年

，

本文編號：2192413