【摘要】：目的添加適量椰纖維(CF)改善聚乳酸(PLA)的力學(xué)性能,以適應(yīng)產(chǎn)品的包裝。方法采用熔融共混法制備不同CF含量的CF/PLA復(fù)合材料。通過力學(xué)性能測試、掃描電子顯微鏡觀察和動態(tài)熱力學(xué)性能測試,探討添加不同含量的堿洗CF對復(fù)合材料力學(xué)性能的影響。結(jié)果與純PLA相比,復(fù)合材料的拉伸強(qiáng)度降低,沖擊強(qiáng)度增大,儲能模量增大,玻璃化轉(zhuǎn)變溫度降低。當(dāng)堿洗CF質(zhì)量分?jǐn)?shù)為3%時(shí),復(fù)合材料的沖擊強(qiáng)度比純PLA增加了24%。結(jié)論添加CF有利于提高復(fù)合材料的力學(xué)性能,堿液浸泡更有利于改善CF和PLA基體的界面相容性。
[Abstract]:Objective to improve the mechanical properties of polylactic acid (PLA) by adding proper amount of coconut fiber (CF). Methods CF/PLA composites with different CF content were prepared by melt blending method. The effects of alkali washing CF on the mechanical properties of composites were investigated by means of mechanical properties test, scanning electron microscopy (SEM) observation and dynamic thermodynamics test. Results compared with pure PLA, the tensile strength, impact strength, storage modulus and glass transition temperature of the composites decreased. When the alkali washing CF content is 3, the impact strength of the composite is 24% higher than that of pure PLA. Conclusion the addition of CF can improve the mechanical properties of the composites, and the soaking of alkali solution can improve the interfacial compatibility between CF and PLA matrix.
【作者單位】： 哈爾濱商業(yè)大學(xué);
【基金】：國家十二五科技支撐計(jì)劃(2011BAD24B01-3) 哈爾濱市科技研發(fā)資金(2014RFXXJ057) 哈爾濱商業(yè)大學(xué)研究團(tuán)隊(duì)支持項(xiàng)目(2016TD005)
【分類號】：TB332

【相似文獻(xiàn)】

相關(guān)期刊論文 前2條

1 L.K.Aggarwal ,徐建榮;水泥膠結(jié)椰纖維板的研究[J];廣東建材;1994年04期

2 ;[J];;年期

相關(guān)會議論文 前1條

1 王玲;劉長紅;;椰纖維網(wǎng)路塹邊坡生態(tài)防護(hù)技術(shù)在湖南省韶山高速公路防護(hù)中的應(yīng)用[A];全國公路生態(tài)綠化理論與技術(shù)研討會論文集[C];2009年

相關(guān)重要報(bào)紙文章 前2條

1 揚(yáng)晉國 編譯;菲律賓將對華出口椰纖維產(chǎn)品[N];亞太經(jīng)濟(jì)時(shí)報(bào);2003年

2 本報(bào)記者 彩霞;在CAFTA建設(shè)進(jìn)程中尋找創(chuàng)業(yè)機(jī)會[N];國際商報(bào);2008年

相關(guān)博士學(xué)位論文 前1條

1 姚嘉;椰纖維增韌復(fù)合材料的設(shè)計(jì)及其性能評價(jià)[D];東北林業(yè)大學(xué);2013年

，

本文編號：2164627