【摘要】：采用溶膠-凝膠模板法,以二合水醋酸鋅為前驅(qū)體,二乙醇胺為穩(wěn)定劑,引入模板劑聚二乙醇獲得多孔氧化鋅薄膜。借助于掃描電鏡、透射電鏡、X射線衍射等手段,對薄膜的微觀組織結(jié)構(gòu)、生長過程和光學(xué)性能進行研究,并分析了模板劑對薄膜生長的溶膠-凝膠過程的影響。研究結(jié)果表明,加入適量模板劑后易獲得多孔結(jié)構(gòu)、結(jié)晶良好的薄膜。隨濃度增加孔道逐漸向蠕蟲狀轉(zhuǎn)變,孔隙率有所下降,多孔薄膜的折射率處于1.5~1.7范圍,透射率可提高到95%以上,薄膜的光學(xué)性能進一步提高。
[Abstract]:Porous zinc oxide thin films were prepared by sol-gel template method with diethanolamine as stabilizer and zinc acetate dihydrate as precursor. By means of scanning electron microscope (SEM), transmission electron microscopy (TEM) and X-ray diffraction (XRD), the microstructure, growth process and optical properties of the films were studied. The influence of the template on the sol-gel process of the films was analyzed. The results show that the films with porous structure and good crystallization are easy to be obtained by adding proper amount of template. With the increase of the concentration of the pore channel, the porosity of the film is decreased, the refractive index of the film is in the range of 1.5 ~ 1.7, the transmittance can be increased to more than 95%, and the optical properties of the film can be further improved.
【作者單位】： 浙江工業(yè)大學(xué)材料科學(xué)與工程學(xué)院;
【分類號】：TB383.2

【相似文獻】

相關(guān)期刊論文 前10條

1 謝來蘇，潘學(xué)軍，胡惠仁，石淑蘭，，隆言泉;紙張光學(xué)性能的某些理論研究[J];中國造紙學(xué)報;1996年00期

2 馬玉天;龔竹青;武俊;李宏煦;陽征會;;影響碲膜光學(xué)性能的因素[J];稀有金屬;2006年03期

3 胡延光,彭紹洪,李偉;高壓薄膜產(chǎn)品光學(xué)性能的影響因素及控制[J];寧夏石油化工;2004年02期

4 姚保知，余錫賓;抗紫外線透明保護膠光學(xué)性能的研究[J];合肥工業(yè)大學(xué)學(xué)報(自然科學(xué)版);1995年S1期

5 杜金成,林文輝,趙修建,劉文,方羅珍;含銀偏振玻璃的制備及光學(xué)性能[J];光學(xué)學(xué)報;1999年05期

6 顏國君;陳光德;呂惠民;;納米六方相氮化鋁的合成和光學(xué)性能研究[J];化學(xué)學(xué)報;2006年16期

7 蔡金輝;高恒p

本文編號：2098190