本文選題：高密度聚乙烯 + 反式-1��； 參考：《青島科技大學(xué)》2017年碩士論文

【摘要】：本文所研究的聚烯烴材料為高密度聚乙烯(HDPE)材料。本文采用反式-1,4-聚異戊二烯(TPI)彈性體作為HDPE的增韌劑,采用機械共混法、動態(tài)硫化法在擠出機中制備HDPE/TPI合金材料,從而來提高HDPE的韌性。通過力學(xué)性能、熱性能及微觀結(jié)構(gòu)相圖等測試,選出HDPE和TPI的最佳配比,并在此基礎(chǔ)上,采用三種納米顆粒材料:納米蒙脫土(nano-MMT)、納米碳酸鈣(nano-CaCO3)、納米二氧化硅(nano-SiO2)來增強HDPE/TPI合金材料的力學(xué)性能耐熱性能。結(jié)果表明:1.當HDPE與TPI的質(zhì)量分數(shù)比為95/5時,HDPE/TPI合金材料具有較高的沖擊強度,合金材料韌性較好,沖擊強度由純HDPE的32.5 kJ/m2提高至51.1 kJ/m2,其他力學(xué)性能和耐熱性能變化不大。2.當HDPE/TPI質(zhì)量分數(shù)比為95/5,硫磺用量為3份,促進劑CZ為1份時,HDPE/TPI動態(tài)硫化合金材料的沖擊強度達到最大值52.8kJ/m2,此時合金材料韌性最佳。當對HDPE韌性要求不是很高的情況下,通過簡單的機械共混即可較大幅度地提高HDPE的韌性,此外,機械共混方法配方簡單,可提高生產(chǎn)效率、降低生產(chǎn)成本。3.當HDPE/TPI質(zhì)量分數(shù)比為95/5時,添加質(zhì)量分數(shù)為3%~5%的納米材料能夠較明顯地增強HDPE/TPI合金材料的力學(xué)性能和耐熱性能,其中納米蒙脫土和納米碳酸鈣的增強效果較好。
[Abstract]:The polyolefin material studied in this paper is high density polyethylene (HDPE). HDPE / TPI alloy materials were prepared by mechanical blending and dynamic vulcanization in order to improve the toughness of HDPE by using the trans-1 / 4-polyisoprene (TPI) elastomer as the toughening agent of HDPE. The optimum ratio of HDPE and TPI was selected by testing mechanical properties, thermal properties and microstructural phase diagrams. The mechanical properties and heat resistance of HDPE / TPI alloy were enhanced by using three kinds of nano-particle materials: nano-montmorillonite nano-MMTT, nano-CaCO3N, nano-SiO2. The result shows that 1: 1. When the mass ratio of HDPE to TPI is 95 / 5, the impact strength of HDPE / TPI alloy is higher and the toughness of the alloy is better. The impact strength of HDPE / TPI alloy is increased from 32.5 KJ / m2 to 51.1 KJ / m2. When the mass ratio of HDPE / TPI is 95 / 5, the amount of sulfur is 3 phr, and the accelerator CZ is 1 phr, the impact strength of HDPE / TPI dynamic vulcanized alloy material reaches the maximum value of 52.8 kJ / m2, and the toughness of the alloy is the best. When the toughness of HDPE is not very high, the toughness of HDPE can be greatly improved by simple mechanical blending. In addition, the formula of mechanical blending method is simple, which can improve the production efficiency and reduce the production cost. When the mass ratio of HDPE / TPI is 95 / 5, the mechanical properties and heat resistance of HDPE / TPI alloy can be obviously enhanced by adding 3% nanomaterials with mass fraction of 3% or 5%, among which nano-montmorillonite and nano-CaCO3 have better reinforcing effect.
【學(xué)位授予單位】：青島科技大學(xué)
【學(xué)位級別】：碩士
【學(xué)位授予年份】：2017
【分類號】：TQ325.12;TB33

【參考文獻】

相關(guān)期刊論文 前10條

1 楊佳偉;;納米材料的制備及應(yīng)用[J];中國戰(zhàn)略新興產(chǎn)業(yè);2017年12期

2 王翔宇;張玉霞;;納米粒子在聚合物共混物中選擇性分布研究進展[J];中國塑料;2017年03期

3 李玉杰;;無機粉體填充HDPE對其綜合性能的影響研究[J];城市地理;2016年24期

4 黃自華;譚宇;胡天輝;;反式-1,4-聚異戊二烯的應(yīng)用研究進展[J];特種橡膠制品;2012年03期

5 王林;侯清麟;楊軍;宋傳江;胡天輝;黃自華;;反式聚異戊二烯的性能及應(yīng)用研究進展[J];湖南工業(yè)大學(xué)學(xué)報;2011年04期

6 李博;魏靜勛;羅吉良;;TPI/NR全鋼子午線輪胎胎面膠性能的研究[J];橡膠科技市場;2009年24期

7 楊丹;黃慧珍;;杜仲膠的研究與發(fā)展[J];世界橡膠工業(yè);2009年07期

8 宋紅梅;杜愛華;趙志超;黃寶琛;;TPI/IR并用膠的性能[J];彈性體;2009年03期

9 楊艷;;塑料——20世紀人類的大杰作[J];發(fā)明與創(chuàng)新(綜合版);2008年02期

10 張利仁;姜明才;劉志軍;張春雨;蔡洪光;;聚乙烯-蒙脫土納米復(fù)合材料的結(jié)構(gòu)與性能[J];石油化工;2006年10期

相關(guān)碩士學(xué)位論文 前1條

1 王瀟;反式-1,4-聚異戊二烯/天然橡膠并用膠的阻尼與低溫性能研究[D];華南理工大學(xué);2014年

，

本文編號：2014546