【摘要】：納米纖絲纖維素(NFC)具有好長寬比、高強度、低密度、可生物降解和可再生等特性,對NFC進行開發(fā)和研究,可拓寬造紙業(yè)中漂白漿的用途。基材是OLED設(shè)備中的第一層,是構(gòu)建柔性電子器件非常重要的部分。本研究以漂白針葉木漿為原料,研究改性的NFC與丙烯酸樹脂ABPE進行復(fù)合制備NFC/ABPE納米復(fù)合材料,探討該復(fù)合材料制備高性能的OLED基材的可行性。主要結(jié)論如下:(1)化學(xué)純化使得紙漿中纖維素含量提高至96.90%。與單獨的機械研磨處理相比,在機械研磨之后進行的高壓均質(zhì)處理對NFC的結(jié)晶度影響不大,NFC的熱穩(wěn)定性也比漂白漿稍高,同時得到的NFC直徑更小、長寬比更大和得率更高。(2)不同的NFC:AC比例改性對NFC中的羥基取代影響較大,當(dāng)NFC:AC比例大于1:6后,葡萄糖單元上的C3、C2和C6上的羥基均被乙�；〈�,且乙�；腘FC無法形成膜。改性對NFC的熱降解過程、Tmax、失重殘余量和透光性影響不大,但改性對NFC膜的CTE、力學(xué)性能和柔韌性影響非常大,當(dāng)NFC:AC比例為1:3時,能較好地保持NFC的力學(xué)性能、柔韌性、結(jié)晶度和降低其熱穩(wěn)定性。(3)NFC與ABPE復(fù)合制得的NFC/ABPE復(fù)合膜表面平整度增加,NFC與ABPE相容粘合性良好,且復(fù)合膜的透光性良好。不同的NFC用量對復(fù)合膜的熱膨脹性、力學(xué)性能和柔韌性的影響最大,且復(fù)合膜的CTE較低均符合國家OLED基板的標(biāo)準(zhǔn)。當(dāng)NFC用量為0.3 g或0.4 g時,復(fù)合膜的力學(xué)性能和柔韌性最優(yōu),與其他基材相比,所制得的復(fù)合膜作為生產(chǎn)OLED基材具有更高的性能。
[Abstract]:Nano-fiber cellulose (NFC) has the characteristics of good aspect ratio, high strength, low density, biodegradability and regeneration. The development and research of NFC can broaden the use of bleached pulp in paper industry. Substrate is the first layer of OLED equipment, and it is very important to construct flexible electronic devices. In this study, the modified NFC and acrylic resin ABPE were used as raw materials to prepare NFC/ABPE nanocomposites, and the feasibility of preparing high performance OLED substrates was discussed. The main conclusions are as follows: (1) Chemical purification increased cellulose content to 96.90%. Compared with the single mechanical grinding treatment, the high pressure homogenization treatment after mechanical grinding has little effect on the crystallinity of NFC and slightly higher thermal stability than that of bleached pulp, and the diameter of NFC is smaller than that of bleached pulp. When the ratio of NFC:AC is more than 1:6, the hydroxyl groups of C _ 3C _ 2 and C _ 6 on glucose unit are replaced by acetyl groups, and the acetylated NFC can not form membrane. The modification had little effect on the thermal degradation process of NFC, weight loss residual amount and light transmittance, but the modification had a great effect on the mechanical properties and flexibility of NFC film. When the NFC:AC ratio was 1:3, the mechanical properties and flexibility of NFC could be better maintained. The surface smoothness of the NFC/ABPE composite film prepared by decreasing its thermal stability. The thermal stability of the NFC/ABPE composite film increased the compatibility and adhesion of NFC/ABPE and ABPE, and the transmittance of the composite film was good. The influence of NFC content on thermal expansion, mechanical properties and flexibility of the composite membrane is the greatest, and the lower CTE of the composite membrane accords with the national standard of OLED substrate. When the amount of NFC is 0.3 g or 0.4 g, the mechanical properties and flexibility of the composite film are the best. Compared with other substrates, the composite film has higher properties as the OLED substrate.
【學(xué)位授予單位】：廣西大學(xué)
【學(xué)位級別】：碩士
【學(xué)位授予年份】：2017
【分類號】：TN383.1;TB33

【參考文獻】

相關(guān)期刊論文 前10條

1 王承遇;盧琪;;顯示器用超薄柔性玻璃[J];玻璃與搪瓷;2016年03期

2 裘國華;章樂;申屠南瑛;;天然纖維素太赫茲和紅外光譜分析研究[J];光譜學(xué)與光譜分析;2016年03期

3 周素坤;毛健貞;許鳳;;微纖化纖維素的制備及應(yīng)用[J];化學(xué)進展;2014年10期

4 陳瑞峰;;柔性超薄玻璃[J];化學(xué)工業(yè);2014年07期

5 李新宇;張明輝;邵朱偉;周云潔;;利用XRD研究乙�；静牡慕Y(jié)晶度和微纖絲角[J];內(nèi)蒙古農(nóng)業(yè)大學(xué)學(xué)報(自然科學(xué)版);2014年04期

6 項秀東;萬小芳;李友明;武書彬;;微纖化纖維的制備及其應(yīng)用的研究進展[J];中國造紙;2013年10期

7 徐琴;李振國;李發(fā)學(xué);俞建勇;;低取代度羥丙基纖維素的制備及影響因素分析[J];東華大學(xué)學(xué)報(自然科學(xué)版);2013年01期

8 傅七蘭;牛敏;謝擁群;;纖維素乙酰化改性研究[J];福建林學(xué)院學(xué)報;2013年01期

9 江澤慧;王漢坤;余雁;田根林;王昊;;植物源微纖化纖維素的制備及性能研究進展[J];世界林業(yè)研究;2012年02期

10 李健;黃慶;李鑫;;PGLA纖維力學(xué)性能與結(jié)晶和取向的關(guān)系[J];化纖與紡織技術(shù);2010年01期

相關(guān)博士學(xué)位論文 前1條

1 于曉慧;新型高性能聚酰亞胺超薄薄膜的結(jié)構(gòu)設(shè)計、制備及研究[D];吉林大學(xué);2011年

相關(guān)碩士學(xué)位論文 前6條

1 楊波;聚乳酸/改性微原纖纖維素復(fù)合材料制備及性能研究[D];大連理工大學(xué);2015年

2 費志賓;基于天然纖維素的環(huán)境功能材料的制備與性質(zhì)研究[D];華南理工大學(xué);2015年

3 胡坤;超薄304不銹鋼片Roll-to-Roll固結(jié)磨料化學(xué)機械拋光輥研制[D];河南工業(yè)大學(xué);2015年

4 潘佳;納米纖維素纖絲/環(huán)氧樹脂復(fù)合材料的研究[D];南京林業(yè)大學(xué);2012年

5 薛瑩瑩;纖維素納米纖絲/丙烯酸樹脂復(fù)合材料的研究[D];南京林業(yè)大學(xué);2012年

6 王紅霞;光固化聚丙烯酸樹脂基復(fù)合材料制備及吸濕性能研究[D];天津大學(xué);2005年

，

本文編號：1873043