本文選題：纖維　切入點(diǎn)：樹脂　出處：《玻璃鋼/復(fù)合材料》2017年02期

【摘要】：對纖維增強(qiáng)樹脂基復(fù)合材料表面金屬化研究進(jìn)行綜述,分別介紹了纖維與樹脂在復(fù)合前的表面金屬化方法,纖維與樹脂復(fù)合后固化前的表面金屬化方法以及纖維與樹脂固化后表面金屬化方法;并且對復(fù)合材料在不同階段的金屬化方法優(yōu)缺點(diǎn)進(jìn)行分析介紹,結(jié)合航空航天領(lǐng)域在復(fù)合材料表面金屬化的需求,分析了不同的金屬化方法在航天復(fù)合材料結(jié)構(gòu)件上的適用性。
[Abstract]:The research on surface metallization of fiber reinforced resin matrix composites was reviewed, and the surface metallization methods of fiber and resin before composite were introduced respectively.The surface metallization method before fiber and resin composite curing and the surface metallization method after fiber and resin curing are introduced, and the advantages and disadvantages of metallization methods in different stages of composite are analyzed.According to the requirement of surface metallization of composite materials in aerospace field, the applicability of different metallization methods in aerospace composite structures is analyzed.
【作者單位】： 上海復(fù)合材料科技有限公司;上海航天樹脂基復(fù)合材料工程技術(shù)研究中心;
【基金】：國家863高科技發(fā)展計(jì)劃(2015AA03A201)
【分類號】：TB332

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 楊瑞法;;塑料表面金屬化——真空裝飾鍍鋁[J];電鍍與涂飾;1984年04期

2 雷風(fēng)徐;;塑料表面金屬化新技術(shù)及其應(yīng)用[J];電鍍與精飾;1984年01期

3 袁國偉;;非導(dǎo)體表面金屬化技術(shù)[J];電子工藝技術(shù);1987年09期

4 索盈;;經(jīng)編織物表面金屬化的方法[J];國外紡織技術(shù)(針織、服裝分冊);1987年18期

5 黃昌萬;玻璃鋼表面金屬化工藝及其討論[J];玻璃鋼/復(fù)合材料;1988年05期

6 張欣;陶瓷表面金屬化的應(yīng)用與研究[J];泰安師專學(xué)報(bào);2000年06期

7 王建,唐勁,梁輝,馮勝雷;非導(dǎo)體表面金屬化[J];電鍍與精飾;2005年03期

8 辛化丹;最新的塑料表面技術(shù)(連載之五)[J];塑料科技;1987年02期

9 ;專利實(shí)例[J];電鍍與精飾;1985年03期

10 辛化丹;最新的塑料表面技術(shù)(連載之六)[J];塑料科技;1987年04期

相關(guān)會(huì)議論文 前9條

1 ，

本文編號：1718077