本文選題：四甲基銨基籠形聚倍半硅氧烷　切入點：殼聚糖　出處：《包裝工程》2016年21期

【摘要】：目的研究以四甲基銨基籠形聚倍半硅氧烷(Octa TMA POSS)為填料,制備殼聚糖基復合膜,對殼聚糖薄膜的水蒸氣阻隔性能和力學性能進行改善。方法采用溶液共混流延法制備復合膜,測定其水蒸氣透過系數(shù)、表面接觸角、溶脹度、溶解度、吸附等溫曲線、拉伸性能、成膜液流變性能、微觀形貌和X射線衍射等。結(jié)果籠形聚倍半硅氧烷的加入可提高復合膜對水分子的阻隔性,尤其是質(zhì)量分數(shù)為3%時,其水蒸氣透過系數(shù)下降了15.9%。同時,殼聚糖薄膜的力學性能也得到改善,在質(zhì)量分數(shù)低于5%時,殼聚糖薄膜的抗拉強度、彈性模量可同時得到提高。結(jié)論四甲基銨基籠形聚倍半硅氧烷的加入可改善殼聚糖薄膜的阻濕性能和力學性能,可大大提升其在食品包裝領域的應用潛力。
[Abstract]:Methods the water vapor transmittance, surface contact angle, swelling, solubility, adsorption isothermal curve, tensile properties, rheological properties, micromorphology and X-ray diffraction were measured.Results the barrier of the composite membrane to water molecules was improved with the addition of cage polysilane, especially when the mass fraction was 3, the water vapor permeability coefficient decreased by 15.9.Conclusion the addition of tetramethylammonium-based polysilsesquioxane can improve the moisture and mechanical properties of chitosan film and enhance its application potential in the field of food packaging.
【作者單位】： 西南大學;
【基金】：國家自然科學基金青年基金(21306154) 中國博士后科學基金(2014M552298)
【分類號】：O636.1;TB383.2

【相似文獻】

相關期刊論文 前3條

1 王瓊生;王世銘;;抗菌手膠的制備[J];福建師范大學學報(自然科學版);2011年06期

2 李倩文;余菁;;幾種增塑劑對殼聚糖薄膜性質(zhì)的比較研究[J];食品科技;2014年08期

3 ;[J];;年期

，

本文編號：1701377