本文選題：聚集誘導(dǎo)發(fā)光材料　切入點(diǎn)：電聚合　出處：《華南師范大學(xué)學(xué)報(bào)(自然科學(xué)版)》2017年02期

【摘要】：以聚集誘導(dǎo)發(fā)光(AIE)材料咔唑基三苯乙烯衍生物(TPCz)為單體,采用循環(huán)伏安法(CV)原位聚合制備了咔唑基三苯乙烯衍生物多孔聚合物薄膜(TPCz-CMPs).利用紅外光譜(FT-IR)、紫外-可見吸收光譜(UV-Vis)、高倍透射電鏡(HR-TEM)等手段對(duì)其結(jié)構(gòu)和形貌進(jìn)行了表征,并對(duì)CMPs薄膜修飾的電極進(jìn)行了循環(huán)優(yōu)安(CV)、恒電流充放電(CP)及交流阻抗(EIS)等電化學(xué)性能測(cè)試.結(jié)果表明,TPCz-CMPs薄膜具有多孔結(jié)構(gòu),在電流密度為4A/g時(shí),TPCz-CMPs薄膜電極的比電容達(dá)到193 F/g,是一種具有應(yīng)用前景的超級(jí)電容器材料.
[Abstract]:The aggregate induced luminescence (AIEs) material, carbazolyl tristyrene derivative (TPCz), was used as monomer. The porous polymer films of carbazolyl tristyrene derivatives were prepared by in situ polymerization with cyclic voltammetry (CV). The structure and morphology of the films were characterized by FTIR, UV-Vis-Vis and HR-TEM. The electrochemical properties of the modified CMPs films were measured by cyclic amperometric charge / discharge (CMPs), constant current charge / discharge (CMPs) and electrochemical impedance spectroscopy (EIS). The results show that TPCz-CMPs thin films have porous structure. When the current density is 4A/g, the specific capacitance of TPCz-CMPs thin film electrode is 193F / g, which is a promising supercapacitor material.
【作者單位】： 華南師范大學(xué)化學(xué)與環(huán)境學(xué)院;
【基金】：國(guó)家自然科學(xué)基金項(xiàng)目(51203054) 博士后科學(xué)基金項(xiàng)目(2014M552192,2015T80906)
【分類號(hào)】：TB383.2;TM53

【相似文獻(xiàn)】

相關(guān)期刊論文 前4條

1 王宇航;張秋禹;馬明亮;尹常杰;寇曉康;;多孔聚合物微球成孔技術(shù)的最新研究進(jìn)展[J];材料導(dǎo)報(bào);2011年11期

2 陳忠元;居亞蘭;張文鋒;朱云峰;李李泉;;一種新型堿性多孔聚合物電解質(zhì)的制備與性能研究[J];材料導(dǎo)報(bào);2009年S1期

3 伍紹飛;喻桂朋;潘春躍;;有機(jī)納米多孔聚合物(NOPs)概述[J];廣州化工;2013年13期

4 ;[J];;年期

相關(guān)會(huì)議論文 前1條

1 李磊;;超臨界二氧化碳發(fā)泡制備納米多孔聚合物薄膜[A];2007年全國(guó)高分子學(xué)術(shù)論文報(bào)告會(huì)論文摘要集（上冊(cè)）[C];2007年

相關(guān)碩士學(xué)位論文 前2條

1 劉獻(xiàn)虎;基于Schiff堿反應(yīng)的有機(jī)多孔聚合物的合成及應(yīng)用[D];蘭州大學(xué);2013年

2 秦新新;模板法制備多孔聚合物材料及其吸附性能的研究[D];哈爾濱工業(yè)大學(xué);2014年

，

本文編號(hào)：1699370