本文選題：中空纖維型自修復　切入點：復合材料　出處：《宇航材料工藝》2017年04期

【摘要】：以5-亞乙基-2-降冰片烯(ENB)和Grubbs催化劑組成的修復系統(tǒng)為修復劑、以外徑為Ф0.9mm的中空玻璃管為載體,通過壓力破壞實驗和三點彎曲實驗研究含有中空玻璃管復合材料的彎曲性能及自修復的效率。結果表明:壓力破壞實驗給試件帶來的損傷程度最大可達到14.67%;已受損的試件在修復系統(tǒng)的作用下,試件的強度能恢復到原強度的99.15%。
[Abstract]:The repair system composed of 5-ethyl-2-norbornene (ENB) and Grubbs catalyst was used as the repair agent, and the hollow glass tube with outer diameter as 0.9mm was used as the carrier. The bending properties and self-repairing efficiency of composite material containing hollow glass tube were studied by pressure failure test and three-point bending test. The results show that the damage degree of the specimen caused by the pressure failure test can reach 14.677.It has been obtained. The damaged specimen is affected by the repair system, The strength of the specimen can be restored to 99.15% of the original strength.
【作者單位】： 天津市現(xiàn)代機電裝備技術重點實驗室;天津工業(yè)大學機械工程學院;
【基金】：國家自然科學基金(11372220)
【分類號】：TB33

【相似文獻】

相關期刊論文 前10條

1 李海燕;張麗冰;李杰;王俊;;外援型自修復聚合物材料研究進展[J];化工進展;2014年01期

2 華凌;;“聰明”水凝膠能瞬間實現(xiàn)切口自修復[J];共產(chǎn)黨員;2012年08期

3 方征平;羊海棠;徐立華;顧嬡娟;佟立芳;許忠斌;;聚合物基復合材料自修復體系的構成與修復機制分析[J];航空材料學報;2006年03期

4 ;浙大制備成功新型自修復材料[J];化工中間體;2012年06期

5 ;自修復仿生涂層幾乎排斥所有液體[J];硅酸鹽通報;2011年06期

6 楊長江;陳國需;陳淑蓮;趙立濤;廖梓s，

本文編號：1674561