本文選題：聚碳酸亞丙酯　切入點(diǎn)：蒙脫土　出處：《湖南工業(yè)大學(xué)》2015年碩士論文　論文類型：學(xué)位論文

【摘要】：聚碳酸亞丙酯(PPC)作為二氧化碳(CO2)與環(huán)氧丙烷(PO)交替共聚的產(chǎn)物,以其優(yōu)良的韌性、可降解性及生物相容性等特點(diǎn),獲得了廣泛的關(guān)注。在實(shí)際應(yīng)用中,PPC因存在熔體黏度過(guò)大、熱穩(wěn)定性和機(jī)械強(qiáng)度較差等問(wèn)題,導(dǎo)致其應(yīng)用范圍受限。為此,本文擬以PPC作為主基材,選用兩種有機(jī)改性的蒙脫土(MMT-DK2,MMT-DK5)和聚乳酸(PLA),制備了PPC/MMT及PPC/PLA/MMT納米復(fù)合材料,以期達(dá)到改善PPC的熱穩(wěn)定性和機(jī)械強(qiáng)度的目的。本文通過(guò)測(cè)試三種工業(yè)化的PPC以確定合適的主基材。結(jié)果表明:DOW PPC和SABIC PPC的碳酸酯基團(tuán)含量極低,且過(guò)低的碳酸酯基團(tuán)含量致使PPC難以降解。因此DOW PPC和SABIC PPC不符合綠色環(huán)保的要求,可以確定天冠PPC為最合適的主基材。進(jìn)一步研究表明:天冠PPC的玻璃化轉(zhuǎn)變溫度(Tg)為30.6℃,且當(dāng)溫度高于110℃時(shí)天冠PPC將出現(xiàn)熱失重。此外天冠PPC在140~170℃溫度范圍內(nèi),流變樣條均較正常。這可以確定天冠PPC的加工溫度為140~170℃。采用天冠PPC和兩種MMT制備了PPC/MMT納米復(fù)合材料。結(jié)果表明這兩種PPC/MMT納米復(fù)合材料均為納米插層結(jié)構(gòu)。其中PPC在MMT-DK2片層中的插層效果更好。此外MMT的添加還提高了PPC的熱穩(wěn)定性和機(jī)械強(qiáng)度,并降低了PPC的熔體黏度,但斷裂伸長(zhǎng)率卻急速下降。綜合上述測(cè)試結(jié)果,添加4wt%MMT-DK2的PPC/MMT納米復(fù)合材料的綜合性能最佳。采用天冠PPC、MMT-DK2和PLA制備了PPC/PLA/MMT納米復(fù)合材料。結(jié)果表明:PPC/PLA/MMT納米復(fù)合材料是“海-島”結(jié)構(gòu)。隨著納米復(fù)合材料中PLA的添加,納米復(fù)合材料的熱穩(wěn)定性、機(jī)械強(qiáng)度及流變性能均得到改善。其中PLA含量為40wt%時(shí),PPC/PLA/MMT納米復(fù)合材料綜合性能最好。
[Abstract]:Polypropylene carbonate (PPC), as a product of alternative copolymerization of carbon dioxide (CO _ 2) and propylene oxide (PO), has gained wide attention due to its excellent toughness, degradability and biocompatibility. Because of the poor thermal stability and mechanical strength, PPC/MMT and PPC/PLA/MMT nanocomposites were prepared by using PPC as the main substrate, two kinds of organic modified montmorillonite (MMT-DK2OMMT-DK5) and polylactic acid (PLA). In order to improve the thermal stability and mechanical strength of PPC, three kinds of industrialized PPC were tested to determine the suitable main substrates. The results showed that the content of carbonates in PPC and SABIC PPC was very low. Therefore, DOW PPC and SABIC PPC do not meet the requirements of green environment, so it can be determined that Tianguan PPC is the most suitable main substrate. Further study shows that the vitrification transition temperature of Tianguan PPC is 30.6 鈩，

本文編號(hào)：1580848