本文選題：紡織材料　切入點：纖維增強復合材料　出處：《中國科技論文》2017年10期 　論文類型：期刊論文

【摘要】：由于在實際生產中棍狀結構比管狀、圓臺狀結構更易于生產,為研究2種纖維增強材料棍件的能量吸收性能,選擇了拉擠成型方式制成復合材料棍件(包括碳纖維增強復合材料棍件和玻璃纖維增強復合材料棍件)。其中,玻璃纖維增強復合材料棍件的制作方式采用在拉擠成型的棍件外層進行編織,然后對整體進行二次固化的混合成型技術以增強玻璃纖維紡織復合材料吸能性。運用實驗研究法,利用萬能實驗機對試樣進行準靜態(tài)壓縮實驗并制成觀察實驗片,將準靜態(tài)壓縮實驗后得到的數(shù)據(jù)計算比能量吸收值,通過光學顯微鏡繪制觀察圖和模式圖分析其破壞機理。一方面探究了外層編織角大小(27°、33°、46°)對玻璃纖維增強復合材料棍件的影響,另一方面對比了相同尺寸的碳纖維增強復合材料棍件和外層編織加固的玻璃纖維增強復合材料棍件的能量吸收性能。研究表明:編織角為27°的棍件能量吸收性能最好(比能量吸收值為54.5J/g),碳纖維增強復合材料棍件(比能量吸收值為131.4J/g)吸能性優(yōu)于玻璃纖維增強復合材料棍件。
[Abstract]:In order to study the energy absorption properties of two kinds of fiber reinforced materials, the rod structure is easier to be produced than the tubular structure in practical production. The pullout molding method is selected to make composite rod (including carbon fiber reinforced composite rod and glass fiber reinforced composite rod). In order to enhance the energy absorption of glass fiber textile composites, the glass fiber reinforced composite rod is made by braiding the outer layer of the extruded rod, and then the secondary solidification of the whole is carried out to enhance the energy absorption of the glass fiber textile composite. The quasi-static compression experiment of the sample was carried out by using a universal experimental machine and the observation experiment was made. The data obtained from the quasi-static compression experiment was calculated as the specific energy absorption value. On the one hand, the influence of the outer braiding angle (27 擄/ 33 擄/ 46 擄) on glass fiber reinforced composite rod was studied. On the other hand, the energy absorption properties of carbon fiber reinforced composite rod with the same size and glass fiber reinforced composite rod reinforced with outer braiding are compared. The results show that the energy absorption property of the bar with a braiding angle of 27 擄is compared. The best (specific energy absorption value is 54.5 J / g), carbon fiber reinforced composite rod (specific energy absorption value is 131.4 J / g) is superior to glass fiber reinforced composite rod.
【作者單位】： 東華大學紡織學院;紡織面料技術教育部重點實驗室;
【基金】：國家自然科學基金資助項目(51302036) 高等學校博士學科點專項科研基金資助項目(20130075120006)
【分類號】：TB332

【相似文獻】

相關期刊論文 前8條

1 高元植;關于玻璃纖維增強復合材料拉擠成型的數(shù)值模型的探討[J];材料開發(fā)與應用;1992年03期

2 陳博;;我國復合材料拉擠成型技術及應用發(fā)展情況分析[J];玻璃鋼/復合材料;2014年09期

3 高元植;玻纖增強復合材料拉擠成型工藝中拉拔速度的估算[J];材料開發(fā)與應用;1993年05期

4 酒卷誠;桑島行正;賈麗霞;;拉擠成型玻璃鋼風力發(fā)熱葉片[J];纖維復合材料;1985年03期

5 孔慶保;;纖維增強塑料拉擠成型工藝綜述[J];纖維復合材料;1985年03期

6 孔慶保;;纖維增強塑料拉擠成型工藝綜述[J];纖維復合材料;1984年01期

7 王輝;;拉擠成型用聚酯樹脂配方的研究[J];纖維復合材料;1987年03期

8 李林,程營,陳浩;拉擠成型FRP路面板構件的研究[J];纖維復合材料;2004年03期

，

本文編號：1576122