發(fā)布時(shí)間：2018-03-01 09:07

  本文關(guān)鍵詞： 納米流體 水基礎(chǔ)液 氮化鈦 潤滑 摩擦　出處：《金屬功能材料》2016年06期 　論文類型：期刊論文

【摘要】：將納米氮化鈦顆粒分散到水基礎(chǔ)液中,加入適量的分散劑,采用兩步法可制備出具有良好分散穩(wěn)定的水基納米氮化鈦流體。在此基礎(chǔ)上,采用單一變量法,用M-200磨損試驗(yàn)機(jī)研究了這種納米流體對(duì)鋼環(huán)的磨損性能,并對(duì)其摩擦潤滑機(jī)理進(jìn)行了分析。結(jié)果表明:摩擦系數(shù)與磨損量隨負(fù)荷的增加表現(xiàn)出先減小后增大的趨勢(shì),并且當(dāng)質(zhì)量分?jǐn)?shù)為1%的PVP與CTMAB混合液作為分散劑、粒徑為20nm且質(zhì)量分?jǐn)?shù)為1%的氮化鈦顆粒、分散介質(zhì)為去離子水時(shí)表現(xiàn)出最佳的潤滑性能。
[Abstract]:The nanometer titanium nitride particles were dispersed into the water base solution, and the proper amount of dispersant was added to the water base solution. The water based nano-titanium nitride fluid with good dispersion and stability could be prepared by two-step method. On the basis of this, a single variable method was adopted. The wear performance of the nano-fluid to steel ring was studied by M-200 wear tester, and the friction lubrication mechanism was analyzed. The results show that the friction coefficient and wear quantity decrease first and then increase with the increase of load. When the mixture of PVP and CTMAB with mass fraction of 1% is used as dispersant and the particle size is 20 nm and the mass fraction of titanium nitride is 1%, the dispersion medium is deionized water, which shows the best lubricating performance.
【作者單位】： 昆明理工大學(xué)機(jī)電工程學(xué)院;
【基金】：國家自然科學(xué)基金項(xiàng)目資助(51165012)
【分類號(hào)】：TQ134.11;TB383.1

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 杜士奎;韓鎧;;鈦精礦氮、碳化產(chǎn)品中氮化鈦、碳化鈦、低價(jià)鈦含量、二氧化鈦的物相分析[J];化工冶金;1983年04期

2 家瑞;建良;玉滿;;氮化鈦鍍膜[J];河北陶瓷;1986年04期

3 朱聯(lián)錫;鄒四維;;高溫氣相合成超細(xì)氮化鈦反應(yīng)速率的研究[J];成都科技大學(xué)學(xué)報(bào);1990年01期

4 陳名浩,沈汝美;超細(xì)碳氮化鈦的分析和評(píng)估[J];分析化學(xué);1993年08期

5 江濤,馬敏莊;氮化鈦的制備及表征[J];分析測(cè)試學(xué)報(bào);1999年04期

6 ;蘭州化物所納米氮化鈦的合成及電化學(xué)特性研究獲進(jìn)展[J];硅酸鹽通報(bào);2011年03期

7 李偉;蔣明學(xué);謝畢強(qiáng);盧紅憲;;碳氮化鈦的制備與應(yīng)用[J];山東陶瓷;2009年03期

8 魯元;龔楠;荊強(qiáng)征;李京京;，

本文編號(hào)：1551276