本文關(guān)鍵詞： 鐵紅 聚磷酸銨 PVC 無鹵阻燃　出處：《消防科學與技術(shù)》2017年09期 　論文類型：期刊論文

【摘要】：通過將鐵紅和聚磷酸銨(APP)復配后加入到PVC中制備阻燃PVC復合材料,研究此阻燃體系對阻燃PVC復合材料的阻燃性能的影響。通過錐形量熱儀、氧指數(shù)、掃描電鏡等表征手段研究鐵紅和聚磷酸銨的復配量對PVC阻燃性能的影響,結(jié)果表明:當鐵紅∶APP∶PVC的配比為5%∶25%∶70%時,阻燃PVC復合材料的阻燃性能最佳,其總熱釋放量、總煙釋放量降低,氧指數(shù)升高。鐵紅的添加可以有效改善形成炭層的表明光滑度和致密度,提升PVC復合材料的阻燃性能。
[Abstract]:The flame retardant PVC composites were prepared by adding iron red and ammonium polyphosphate (app) into PVC to study the effect of the flame retardant system on the flame retardant properties of PVC composites. The effects of the mixture of iron red and ammonium polyphosphate on the flame retardancy of PVC were studied by SEM. The results showed that when the ratio of iron red to PVC was 5: 25: 70%, the flame retardant PVC composite had the best flame retardant property and its total heat release was the best. The total smoke emission decreased and the oxygen index increased. The addition of iron red could effectively improve the smoothness and density of the carbon layer and improve the flame retardancy of PVC composites.
【作者單位】： 懷化市消防支隊;
【分類號】：TB33

【相似文獻】

相關(guān)期刊論文 前10條

1 趙永生;王克儉;朱復華;薛平;包文春;趙雁鳴;;蒙脫土/硅烷改性木粉/PVC復合材料[J];復合材料學報;2007年03期

2 李春霞;沈梅;辛振祥;;杜仲翅果殼粉/PVC復合材料力學性能研究[J];塑料包裝;2014年03期

3 王平華;王賀宜;唐龍祥;張斌;程文超;梁永標;;碳納米管/PVC復合材料的制備及表征[J];高分子材料科學與工程;2008年01期

4 張玲;牛建華;孫水升;;納米CaCO_3的接枝改性及其填充PVC復合材料的性能[J];聚氯乙烯;2008年08期

5 魏守左,陳延勇,嚴瑞芳;以杜仲膠渣作填料的PVC復合材料的研究[J];材料科學進展;1988年01期

6 曾曉飛,陳建峰,趙紅英;納米CaCO_3-PVC復合材料微觀結(jié)構(gòu)和力學性能研究[J];北京化工大學學報(自然科學版);2001年04期

7 葉林忠，鄭魯光，，趙連軍，吳其曄;短玻璃纖維/R─PVC復合材料的紅外光譜和聲發(fā)射分析[J];青島化工學院學報;1995年03期

8 曾曉飛,陳建峰,王國全;納米CaCO_3/PVC復合材料結(jié)構(gòu)形態(tài)與沖擊性能[J];高�；瘜W工程學報;2002年02期

9 孫水升,李春忠,張玲,曹宏明;CPE對納米CaCO_3增韌PVC復合材料界面和性能的影響[J];過程工程學報;2005年05期

10 董鵬飛;韓婧;邵啟偉;成榮明;;ZnO納米棒/PVC復合材料的光催化性能研究[J];華東師范大學學報(自然科學版);2009年05期

相關(guān)博士學位論文 前1條

1 岳小鵬;木質(zhì)素在PVC復合材料中的應(yīng)用研究[D];華南理工大學;2011年

相關(guān)碩士學位論文 前2條

1 萬正龍;竹粉/PVC復合材料的制備及性能研究[D];華中農(nóng)業(yè)大學;2010年

2 劉建超;疏水聚磷酸銨及耐水IFR-PP復合材料性能研究[D];東北林業(yè)大學;2015年

本文編號：1499915