本文關(guān)鍵詞： 聚氨酯 復(fù)合材料 韌性 強度 蒙脫土 芐基化　出處：《上海紡織科技》2017年06期 　論文類型：期刊論文

【摘要】：芐基化棉稈皮纖維因熱熔粘度過高,無法有效地浸潤纖維,故其自增強復(fù)合材料力學(xué)性能受到影響。分別采用聚氨酯(TPU)和蒙脫土(MMT)與芐基化棉稈皮纖維混煉制備復(fù)合材料,以提高復(fù)合材料的韌性和強度;利用SEM分別研究了添加TPU和MMT后復(fù)合材料的微觀結(jié)構(gòu),探究TPU和MMT的用量變化對復(fù)合材料力學(xué)性能的影響及原因。結(jié)果表明:TPU和MMT對芐基化棉稈皮纖維型復(fù)合材料具有良好的增韌增強效果;當(dāng)TPU用量在20%以上時,增韌效果較好,但不能同時增強和增韌;而MMT用量在4%時,可以同時獲得較好的增韌和增強效果。
[Abstract]:Benzylated cotton stalk skin fiber can not effectively infiltrate the fiber because of its high hot melt viscosity. Therefore, the mechanical properties of the self-reinforced composites were affected. The composites were prepared by mixing polyurethane (TPU) and montmorillonite (MMT) with benzylated cotton stalk skin fibers. To improve the toughness and strength of composites; The microstructure of the composites after the addition of TPU and MMT was studied by SEM. The effects of TPU and MMT contents on the mechanical properties of the composites were investigated. The results showed that TPU and MMT had a good toughening and reinforcing effect on benzylated cotton stalk skin fiber composites. When the amount of TPU is more than 20%, the toughening effect is better, but it can not be strengthened and toughened at the same time. When the dosage of MMT is 4, good toughening and strengthening effect can be obtained at the same time.
【作者單位】： 大連工業(yè)大學(xué)紡織與材料工程學(xué)院;
【分類號】：TB332
【正文快照】： 近年來,以塑化天然植物纖維作為基體,制備天然纖維增強塑化植物纖維基復(fù)合材料引起了人們的關(guān)注,尤以芐基化和氰乙基化改性纖維的研究取得了很大的進展[1-3]。該復(fù)合材料不但基體和增強纖維來源于植物纖維,價格低廉又環(huán)境友好,而且塑化后天然纖維與增強纖維化學(xué)成分相近,復(fù)合

【相似文獻】

相關(guān)碩士學(xué)位論文 前3條

1 夏勝娟;基于蒸汽閃爆預(yù)處理的棉稈皮纖維及其PBS復(fù)合材料制備[D];江南大學(xué);2017年

2 趙春麗;棉稈皮纖維增強聚丙烯復(fù)合材料的制備及性能研究[D];新疆大學(xué);2013年

3 王博;改性棉桿皮/聚乳酸阻燃復(fù)合板材性能研究[D];大連工業(yè)大學(xué);2015年

，

本文編號：1462923