【摘要】：采用沉淀法與水熱法合成了納米棒狀載銀羥基磷灰石(Ag-HA)顆粒。研究不同合成方法和載銀量時(shí)Ag-HA晶體結(jié)構(gòu)、形貌及抗菌性能。結(jié)果表明:水熱法合成的Ag-HA長徑比高、分散性好,產(chǎn)物結(jié)晶度高、晶粒尺寸大,晶胞參數(shù)更小。沉淀法70℃時(shí),Ag-HA平均晶粒尺寸為(22.7±0.7)nm;水熱法180℃時(shí),平均晶粒尺寸為(50.7±0.9)nm。銀的引入會增大產(chǎn)物晶粒尺寸及晶胞參數(shù),當(dāng)載銀量為1.30%時(shí),平均晶粒尺寸為(53.7±0.9)nm,晶胞參數(shù)a=0.9465nm,c=0.6970nm。產(chǎn)物與大腸桿菌(E.coli)和金黃色葡萄球菌(S.aureus)共培養(yǎng)后結(jié)果顯示,Ag-HA對兩種實(shí)驗(yàn)菌均表現(xiàn)出良好的殺菌性能,不同載銀量Ag-HA在1,3,6,12,24h后的殺菌率均為100%。
[Abstract]:Nanocrystalline silver loaded hydroxyapatite (Ag-HA) particles were synthesized by precipitation and hydrothermal method. The crystal structure of Ag-HA was studied under different synthesis methods and silver loading. The results showed that the Ag-HA synthesized by hydrothermal method had high aspect ratio, good dispersion, high crystallinity, large grain size and smaller unit cell parameters. The average grain size of Ag-HA is 22. 7 鹵0. 7 nm. At 180 鈩，