本文關(guān)鍵詞：富勒烯納米二硫化鉬的制備　出處：《中國(guó)鉬業(yè)》2016年02期 　論文類型：期刊論文

  更多相關(guān)文章： 二硫化鉬 IF-納米二硫化鉬 制備 應(yīng)用

【摘要】：利用鉬酸銨和硫化鈉為原料,聚乙二醇為分散劑,用1∶1鹽酸溶液控制體系p H值1~2,制備出非晶態(tài)三硫化鉬。然后在氫氣氛下煅燒三硫化鉬得到IF-納米二硫化鉬。通過(guò)單因素條件實(shí)驗(yàn)研究了反應(yīng)溫度、反應(yīng)時(shí)間、摩爾配比、分散劑用量等因素對(duì)三硫化鉬轉(zhuǎn)化率的影響;利用正交實(shí)驗(yàn)得出制備三硫化鉬優(yōu)化工藝條件。經(jīng)X射線衍射儀(XRD)與透鏡電子顯微鏡(TEM)表征顯示,由三硫化鉬制備的IF-納米二硫化鉬的粒徑約在30~60 nm左右。
[Abstract]:Using ammonium molybdate and sodium sulfide as raw materials and polyethylene glycol as dispersant, the pH value of the system was controlled with 1: 1 hydrochloric acid solution. Amorphous molybdenum trisulfide was prepared. Then molybdenum trisulfide was calcined in hydrogen atmosphere to obtain IF-nano molybdenum disulfide. The reaction temperature, reaction time and molar ratio were studied by single factor experiments. The effect of dispersant dosage on the conversion of molybdenum trisulfide; The optimum conditions for preparation of molybdenum trisulfide were obtained by orthogonal experiment. The results were characterized by X-ray diffractometer (XRD) and lens electron microscope (TEM). The particle size of IF-nano molybdenum disulfide prepared from molybdenum trisulfide is about 30 ~ 60 nm.
【作者單位】： 河南化工職業(yè)學(xué)院;
【分類號(hào)】：TB383.1;TQ136.12
【正文快照】： 163.com0引言二硫化鉬(Mo S2)為藍(lán)灰色至黑色固體粉末,具有金屬光澤,觸之有滑膩感,是從天然輝鉬礦經(jīng)提純而得到的一種礦物質(zhì)。二硫化鉬與石墨相似,屬于六方晶系的層狀結(jié)構(gòu)[1-2]如圖1、圖2所示。Mo S2晶體是由S-Mo-S3個(gè)平面單元層所組成,單元層中每個(gè)鉬原子被六個(gè)硫原子呈三棱

【相似文獻(xiàn)】

相關(guān)期刊論文 前3條

1 胡坤宏;范廣能;管航敏;韓成良;;納米二硫化鉬的制備及AFM表征[J];合肥學(xué)院學(xué)報(bào)(自然科學(xué)版);2005年04期

2 胡獻(xiàn)國(guó),沃恒洲,胡坤宏,韓效釗;用硫化鈉制備二硫化鉬納米顆粒[J];機(jī)械工程材料;2004年01期

3 ;[J];;年期

相關(guān)碩士學(xué)位論文 前1條

1 胡坤宏;納米二硫化鉬制備工藝及其摩擦學(xué)性能研究[D];合肥工業(yè)大學(xué);2004年

，

本文編號(hào)：1391356