本文選題：混凝土 + 接觸特性��； 參考：《科學技術與工程》2017年28期

【摘要】：為分析混凝土與混凝土接觸特性,采用直剪試驗和單軸壓縮試驗分別研究了混凝土與混凝土接觸法向和切向接觸特性。試驗結(jié)果表明接觸面剪切應力隨剪切位移變化過程可分為彈性變形階段、塑性硬化變形階段;剪切應力達到峰值后,接觸面仍處于較高的應力狀態(tài),試件局部位置出現(xiàn)破壞。Archhard非線性摩擦冪次準則能夠較好的描繪出剪切應力峰值與軸向應力的關系,為相似接觸條件問題剪切應力峰值的估計和預測提供依據(jù)。在混凝土未產(chǎn)生破壞時,接觸面的法向和切向接觸剛度可分別取值為28.95、12.77 MPa/mm,為相似接觸條件的分析計算提供參考。
[Abstract]:In order to analyze the contact characteristics between concrete and concrete, direct shear test and uniaxial compression test were used to study the normal and tangential contact characteristics of concrete and concrete respectively. The experimental results show that the process of shear stress variation with shear displacement can be divided into elastic deformation stage and plastic hardening deformation stage, and the contact surface is still in a high stress state when the shear stress reaches its peak. The relationship between the shear stress peak and the axial stress can be well described by the Archhard nonlinear friction power criterion, which provides a basis for estimating and predicting the shear stress peak in similar contact conditions. The normal and tangential contact stiffness of the contact surface is 28.95 ~ 12.77 MPA / mm, which provides a reference for the analysis and calculation of the similar contact conditions.
【作者單位】： 中國礦業(yè)大學(北京)深部巖土力學與地下工程國家重點實驗室力學與建筑工程學院;
【基金】：國家自然科學基金(U1261212,41172116)資助
【分類號】：TU528

【相似文獻】

相關期刊論文 前1條

1 盧朝陽;;淺談粉磨工藝的兩“度”對水泥質(zhì)量的影響[J];科技與企業(yè);2014年05期

相關碩士學位論文 前1條

1 劉恒;粗骨料對混凝土中氯離子擴散影響試驗研究[D];天津大學;2016年

，

本文編號：2009799