本文選題：高強混凝土 + 荷載歷史�。� 參考：《煙臺大學(xué)》2017年碩士論文

【摘要】：高強混凝土在長期的使用過程中因施工不當、自然災(zāi)害、混凝土意外受荷載等原因會使混凝土遭受不同程度的損傷,而混凝土結(jié)構(gòu)也難免會處在化學(xué)介質(zhì)、大氣中的CO2等侵蝕條件下工作,結(jié)構(gòu)的耐久性及力學(xué)性能均會發(fā)生劣化。因而研究在歷史荷載與環(huán)境因素聯(lián)合作用下對高強混凝土的損傷作用有重要意義。本文的主要工作如下:(1)對尺寸為100mm?100mm?300 mm經(jīng)歷不同程度軸壓荷載歷史的高強混凝土試件進行硫酸鹽長期浸泡和干濕循環(huán)試驗,并在侵蝕180d后對其進行單軸壓縮試驗。分析歷史荷載水平、硫酸鹽濃度、侵蝕方式對混凝土質(zhì)量、峰值應(yīng)力、峰值應(yīng)變、彈性模量、應(yīng)力-應(yīng)變?nèi)�等的影響。結(jié)果表明:高強混凝土隨著硫酸鹽溶液濃度的增加,長期浸泡下,峰值應(yīng)變先減小后增加,干濕循環(huán)條件下則持續(xù)增加;其峰值應(yīng)力、彈性模量在長期浸泡條件下,有先增加后降低的趨勢,而干濕循環(huán)條件下則為持續(xù)下降。兩種侵蝕方式下,隨著歷史荷載的增加,峰值應(yīng)力降低、峰值應(yīng)變增加、彈性模量減小,但變化的幅度較小。(2)對尺寸為100mm?100mm?300 mm的高強混凝土試塊在疲勞歷史荷載與碳化侵蝕聯(lián)合作用后進行試驗研究,研究不同疲勞歷史荷載水平、碳化齡期對高強混凝土的碳化深度、峰值應(yīng)力、峰值應(yīng)變、彈性模量、應(yīng)力-應(yīng)變?nèi)�等的影響,結(jié)果表明:隨著碳化時間的增加,碳化深度逐漸增加,彈性模量增加,峰值應(yīng)力逐漸增加,峰值應(yīng)變降低,且疲勞歷史荷載越大,峰值應(yīng)力隨碳化時間增長的速度越大,但峰值應(yīng)變變化不明顯。單一疲勞歷史荷載作用下,隨著疲勞歷史荷載的增加,高強混凝土的峰值應(yīng)力變小,峰值應(yīng)變增大,但隨著碳化時間的增加,后期的這種趨勢在逐漸的縮小。(3)研究了歷史荷載與環(huán)境因素聯(lián)合作用后的損傷特性,通過提出聯(lián)合因子K與延性損傷因子△D,表明荷載歷史損傷與硫酸鹽侵蝕、碳化侵蝕等環(huán)境因素聯(lián)合作用下對混凝土損傷是促進作用,且各因素水平越高,這種聯(lián)合作用后加速損傷作用一般越是明顯。
[Abstract]:During the long-term use of high strength concrete, due to improper construction, natural disasters and unexpected loads on concrete, the concrete will suffer different degrees of damage, and the concrete structure will inevitably be in the chemical medium. The durability and mechanical properties of the structure will deteriorate under the condition of CO2 erosion in the atmosphere. Therefore, it is of great significance to study the damage of high strength concrete under the combination of historical load and environmental factors. The main work of this paper is as follows: (1) High strength concrete specimens whose size is 100mm?100mm?300 mm have been subjected to long term soaking and wet and dry cycling tests with different axial compression loads, and uniaxial compression tests have been carried out after 180 days of erosion. The effects of historical load level, sulfate concentration and erosion mode on concrete quality, peak stress, peak strain, elastic modulus, stress-strain curve and so on are analyzed. The results show that with the increase of sulfate concentration, the peak strain decreases first and then increases, and the peak stress and modulus of elasticity increase under the condition of long-term immersion. There was a tendency to increase at first and then to decrease, while under dry and wet cycle conditions, it continued to decrease. With the increase of historical load, the peak stress decreases, the peak strain increases and the elastic modulus decreases. However, the range of variation is small. (2) after the combined action of fatigue history load and carbonation erosion, the carbonation depth of high strength concrete with different fatigue historical load level and carbonation age is studied. The effects of peak stress, peak strain, elastic modulus, stress-strain curve and so on. The results show that with the increase of carbonation time, the carbonation depth increases gradually, the elastic modulus increases, the peak stress increases, and the peak strain decreases. The higher the fatigue history load, the faster the peak stress increases with the carbonization time, but the change of peak strain is not obvious. Under the action of single fatigue history load, with the increase of fatigue history load, the peak stress of high strength concrete becomes smaller, the peak strain increases, but with the increase of carbonization time, In the later period, the damage characteristics of historical load combined with environmental factors were studied. By proposing the combined factor K and ductile damage factor D, it was shown that historical load damage and sulfate erosion. Under the combined action of environmental factors such as carbonization erosion, the damage of concrete is promoted, and the higher the level of each factor is, the more obvious the accelerated damage is after the combined action.
【學(xué)位授予單位】：煙臺大學(xué)
【學(xué)位級別】：碩士
【學(xué)位授予年份】：2017
【分類號】：TU528.31

【參考文獻】

相關(guān)期刊論文 前10條

1 解詠平;賈磊;李慎奎;范進勝;;高性能混凝土抗硫酸鹽侵蝕的試驗研究[J];建筑結(jié)構(gòu);2017年06期

2 逯靜洲;國力;劉亞;朱孔峰;;疲勞荷載和碳化聯(lián)合作用下混凝土損傷特性試驗研究[J];混凝土;2017年01期

3 姜磊;牛荻濤;;硫酸鹽侵蝕與干濕循環(huán)下混凝土本構(gòu)關(guān)系研究[J];中國礦業(yè)大學(xué)學(xué)報;2017年01期

4 梁巖;羅小勇;史艷;;反復(fù)荷載下碳化混凝土力學(xué)性能及本構(gòu)關(guān)系研究[J];湖南大學(xué)學(xué)報(自然科學(xué)版);2016年09期

5 徐善華;李安邦;崔煥平;劉小微;;單調(diào)荷載作用下碳化混凝土應(yīng)力-應(yīng)變關(guān)系試驗研究[J];建筑結(jié)構(gòu);2016年06期

6 徐善華;李安邦;崔煥平;劉小微;;反復(fù)荷載作用下碳化混凝土應(yīng)力-應(yīng)變關(guān)系試驗[J];哈爾濱工業(yè)大學(xué)學(xué)報;2015年12期

7 徐善華;孔德亮;李安邦;朱文治;;完全碳化混凝土單軸受壓力學(xué)性能試驗研究[J];西安建筑科技大學(xué)學(xué)報(自然科學(xué)版);2015年02期

8 趙慶新;許宏景;閆國亮;;應(yīng)力損傷對混凝土抗碳化性能的影響[J];建筑材料學(xué)報;2013年03期

9 史慶軒;王南;王秋維;門進杰;;高強箍筋約束高強混凝土軸心受壓本構(gòu)關(guān)系研究[J];工程力學(xué);2013年05期

10 邢明亮;關(guān)博文;陳拴發(fā);盛燕萍;熊銳;;硫酸鹽腐蝕與疲勞荷載聯(lián)合作用下混凝土劣化特性[J];建筑材料學(xué)報;2013年02期

相關(guān)博士學(xué)位論文 前3條

1 曹健;軸壓荷載下干濕循環(huán)—硫酸鹽侵蝕耦合作用混凝土長期性能[D];北京交通大學(xué);2013年

2 高潤東;復(fù)雜環(huán)境下混凝土硫酸鹽侵蝕微—宏觀劣化規(guī)律研究[D];清華大學(xué);2010年

3 金祖權(quán);西部地區(qū)嚴酷環(huán)境下混凝土的耐久性與壽命預(yù)測[D];東南大學(xué);2006年

相關(guān)碩士學(xué)位論文 前3條

1 邵艷明;經(jīng)歷荷載歷史后硫酸鈉侵蝕下混凝土損傷性能研究[D];煙臺大學(xué);2016年

2 史艷;損傷混凝土受壓本構(gòu)關(guān)系試驗研究[D];中南大學(xué);2013年

3 王琴;混凝土在干濕循環(huán)與硫酸鹽侵蝕雙重因素作用下的損傷研究[D];揚州大學(xué);2008年

，

本文編號：1901218