本文選題：織物增強水泥基復(fù)合材料 + 碳纖維織物　； 參考：《湖南大學學報(自然科學版)》2017年11期

【摘要】：采用軸向拉伸試驗研究了碳纖維織物增強水泥基復(fù)合材料(TRC)的靜力力學性能,試驗工況考慮了配網(wǎng)率、短切鋼纖維以及碳纖維織物上的預(yù)拉力3個因素.試驗結(jié)果表明:沒有摻加短切鋼纖維的薄板,隨著配網(wǎng)率的增加,碳纖維織物利用率降低,試驗過程中纖維層與水泥基層逐漸分離,最終薄板發(fā)生剝離破壞;對碳纖維織物施加預(yù)拉力能使薄板的開裂應(yīng)力提高,從而提高TRC構(gòu)件的正常使用壽命;在薄板中摻入短切鋼纖維有助于提高其界面性能,進而使薄板抗拉強度、極限應(yīng)變均得以提高;與施加預(yù)拉力相比,摻入短切鋼纖維對薄板力學性能的改善更加顯著;對碳纖維織物施加預(yù)拉力的同時在薄板中摻入1%的短切鋼纖維可顯著提高碳纖維的利用率,薄板破壞時碳纖維被完全拉斷.
[Abstract]:The static mechanical properties of carbon fiber reinforced cement matrix composites (TRC) were studied by axial tensile test. Three factors were taken into account in the test conditions: distribution ratio, short cut steel fiber and pretensile force on carbon fiber fabric. The test results show that the carbon fiber fabric utilization ratio decreases with the increase of the distribution ratio, and the fiber layer is gradually separated from the cement base during the test, and finally the sheet is peeled and destroyed. Applying pretensile force to carbon fiber fabric can increase the cracking stress of thin plate, thus improve the normal service life of TRC member, and adding short cut steel fiber into thin plate can improve the interfacial properties and further make the sheet tensile strength. Compared with pretensile force, the mechanical properties of thin plate were improved by adding short cut steel fiber. When pretensile force is applied to carbon fiber fabric and 1% short cut steel fiber is added into thin sheet, the utilization ratio of carbon fiber can be improved significantly. When the sheet is destroyed, carbon fiber is completely broken.
【作者單位】： 湖南大學工程結(jié)構(gòu)損傷診斷湖南省重點實驗室;湖南大學土木工程學院;
【基金】：國家自然科學基金資助項目(51378199) 長沙市科技計劃項目(kq1701032)~~
【分類號】：TU599

【相似文獻】

相關(guān)期刊論文 前5條

1 ;德國推出“米袋子“防震法[J];發(fā)明與創(chuàng)新(綜合版);2009年07期

2 潘永燦;荀勇;;纖維織物增強混凝土薄板抗折強度試驗研究[J];混凝土與水泥制品;2006年04期

3 姜亞明,劉良森,葉雪康;建筑物補強材料用經(jīng)編單軸向碳纖維織物[J];針織工業(yè);2004年03期

4 邱洪林;姜裕;;碳纖維織物補強加固混凝土結(jié)構(gòu)研究[J];工程建設(shè)與設(shè)計;2011年04期

5 呂立斌;荀勇;;預(yù)應(yīng)力碳纖維織物增強混凝土簿板中織物的設(shè)計與生產(chǎn)[J];鹽城工學院學報(自然科學版);2010年04期

相關(guān)會議論文 前2條

1 趙彤;謝劍;戴自強;張景明;鄭宏;劉明國;;碳纖維織物補強加固混凝土結(jié)構(gòu)研究(綜述)[A];第九屆全國結(jié)構(gòu)工程學術(shù)會議論文集第Ⅰ卷[C];2000年

2 徐世p，

本文編號：1858609