本文關(guān)鍵詞：滲透結(jié)晶型水泥基防滲材料的制備及防滲機(jī)理研究　出處：《中北大學(xué)》2017年碩士論文　論文類型：學(xué)位論文

  更多相關(guān)文章： 滲透結(jié)晶 水泥基防滲材料 力學(xué)性能 微觀結(jié)構(gòu) 防水機(jī)理

【摘要】：傳統(tǒng)的防滲材料由于毒性大、耐久性差以及和混凝土基體適應(yīng)性不好等原因較適應(yīng)建筑業(yè)發(fā)展需求。滲透結(jié)晶型水泥基防水材料(CCCW)作為一種新型、綠色環(huán)保的防滲材料,不僅具有抗?jié)B功能,還具有滲透結(jié)晶和自修復(fù)等多種優(yōu)良特性,被廣泛應(yīng)用于各種抗?jié)B、防水工程中。本課題通過大量閱讀文獻(xiàn),在充分了解水泥基滲透結(jié)晶型防水材料的作用機(jī)理和應(yīng)用研究基礎(chǔ)上,根據(jù)其反應(yīng)機(jī)理選擇若干種化學(xué)物質(zhì)和其它的輔助材料,在確定輔助材料摻量基礎(chǔ)上,利用正交試驗(yàn)方法,研究不同組分化學(xué)材料對(duì)防水性能的影響,優(yōu)化并制備出了一種以硅酸鹽水泥及為基礎(chǔ)、以礦物摻合料為輔助材料、以化學(xué)物質(zhì)為核心材料的滲透結(jié)晶型水泥基防水材料。同時(shí)通過X射線衍射、掃描電鏡、熱重-差熱等微觀測(cè)試手段,對(duì)所制備的防水材料防水機(jī)理進(jìn)行微觀機(jī)理分析,從微觀上角度分析所制備水泥基滲透結(jié)晶型防滲材料作用機(jī)理。本文通過三方面實(shí)驗(yàn)研究,得出以下結(jié)論:(1)通過水泥凈漿物理、力學(xué)性能及膠砂力學(xué)性能研究,得出制備防滲材料所需的礦物摻合料(輔助材料)最佳摻量比例:硅粉:礦渣:粉煤灰:減水劑=10%:12%:10%:0.4%。(2)通過正交試驗(yàn),由砂漿抗壓強(qiáng)度、砂漿相對(duì)滲透系數(shù)、砂漿抗氯離子系數(shù)及砂漿抗碳化高度四個(gè)指標(biāo),得到所制備的防滲材料所需的活性化學(xué)物質(zhì)占膠凝材料質(zhì)量為5.3%;其活性材料組成比例為組分A:組分B:組分C:組分D=10:200:300:20。(3)通過微觀形貌分析,添加防滲材料料后,較空白砂漿試件相比,水化產(chǎn)物中出現(xiàn)了更多的針狀、棒狀的鈣礬石、碳酸鈣等結(jié)晶體及膠凝材料,同時(shí)添加防滲材料后,防滲材料中的化學(xué)物質(zhì)能進(jìn)一步促進(jìn)水泥水化反應(yīng),使得砂漿結(jié)構(gòu)更加致密。
[Abstract]:The traditional impervious materials are more suitable for the development of the construction industry because of their high toxicity, poor durability and poor adaptability to the concrete matrix. As a new type of waterproofing material, the permeable crystalline cement-based waterproofing material is a new type. Green anti-seepage materials not only have anti-seepage function, but also have many excellent properties such as permeation crystallization and self-repair, which have been widely used in various anti-seepage and waterproofing projects. On the basis of fully understanding the action mechanism and application research of cement-based permeable crystalline waterproof material, several kinds of chemical substances and other auxiliary materials are selected according to its reaction mechanism, on the basis of determining the amount of auxiliary material. By means of orthogonal test, the influence of chemical materials of different components on waterproofing performance was studied, and a kind of Portland cement and mineral admixture as auxiliary material was optimized and prepared. The permeable crystalline cement-based waterproofing material with chemical substance as the core material. At the same time, the microcosmic test means such as X-ray diffraction, scanning electron microscope, thermogravimetry and differential heat were used. The waterproofing mechanism of the waterproofing material is analyzed. The mechanism of the cement-based permeable crystalline anti-seepage material is analyzed from the microcosmic point of view. In this paper, three aspects of experimental study are carried out. Draw the following conclusion: (1) through the cement paste physical, mechanical properties and cemented sand mechanical properties. The optimum ratio of mineral admixture (auxiliary material) needed to prepare impervious material is obtained: silica fume: slag: fly ash: water reducer 10: 12: 10: 0.4. 2) through orthogonal test. According to the compressive strength of mortar, the relative permeability coefficient of mortar, the anti-carbonation height of mortar, it is obtained that the active chemical material used in the preparation is 5.3% of the cementitious material. The composition ratio of active material is component A: component B: component C: component D10: 200: 30020.03) after adding impermeable material through microscopic morphology analysis. Compared with the blank mortar samples, there are more needle-like, rod-like ettringite and calcium carbonate crystals and cementitious materials in the hydration products. The chemical in the impervious material can further promote the hydration reaction of cement and make the mortar structure denser.
【學(xué)位授予單位】：中北大學(xué)
【學(xué)位級(jí)別】：碩士
【學(xué)位授予年份】：2017
【分類號(hào)】：TU57

【參考文獻(xiàn)】

相關(guān)期刊論文 前10條

1 朱海燕;;防水卷材在屋頂防水施工中的應(yīng)用[J];黑龍江科技信息;2016年30期

2 石振武;柳明亮;;電通量指標(biāo)快速評(píng)價(jià)混凝土抗凍性試驗(yàn)研究[J];公路交通科技;2014年12期

3 劉亞明;;防水混凝土結(jié)構(gòu)滲漏原因及控制措施[J];山西建筑;2013年08期

4 楊海榮;張平;;地下工程新型防水材料構(gòu)造措施研究[J];新型建筑材料;2013年01期

5 何小芳;張亞爽;李小慶;劉玉飛;曹新鑫;;水泥水化產(chǎn)物的熱分析研究進(jìn)展[J];硅酸鹽通報(bào);2012年05期

6 劉杰勝;余俊;張宗旺;李剛;;水泥滲透結(jié)晶型防水材料研究[J];武漢工業(yè)學(xué)院學(xué)報(bào);2012年03期

7 喻驍;胡愛宇;;氫氧化鈉與硅酸鈉對(duì)礦渣活性的激發(fā)效果淺析[J];浙江建筑;2012年07期

8 吳建華;鄧少楨;張加運(yùn);何兵;鐘佩華;孫錦;;水泥基滲透結(jié)晶材料對(duì)提高混凝土抗碳化性能影響研究[J];混凝土;2011年10期

9 鮑旺;韓冬冬;倪坤;鐘世云;;水泥基滲透結(jié)晶型防水涂料作用機(jī)理研究進(jìn)展和分析[J];新型建筑材料;2011年09期

10 張翠;萬(wàn)毅;;水泥基滲透結(jié)晶型防水材料的研究[J];才智;2010年19期

相關(guān)碩士學(xué)位論文 前4條

1 李榮江;水泥抗?jié)B復(fù)合涂層的配方優(yōu)化研究[D];齊齊哈爾大學(xué);2012年

2 王平;基于性能的水泥基滲透結(jié)晶防水材料研究[D];安徽工業(yè)大學(xué);2011年

3 陳光耀;水泥基滲透結(jié)晶型防水劑及其裂縫自修復(fù)性能的研究[D];華南理工大學(xué);2010年

4 劉紅葉;水泥基滲透結(jié)晶型防水材料的研究[D];西安建筑科技大學(xué);2004年

，

本文編號(hào)：1431459