本文關(guān)鍵詞：鋼纖維在混凝土沖擊斷面的分布與統(tǒng)計分析　出處：《硅酸鹽通報》2017年11期 　論文類型：期刊論文

  更多相關(guān)文章： 鋼纖維混凝土 抗沖擊 分散系數(shù) 威布爾分布 失效概率

【摘要】：采用自制落錘沖擊試驗(yàn)裝置,對5組鋼纖維體積摻量分別為0、0.5%、0.8%、1.0%、1.2%的鋼纖維混凝土圓餅狀試件進(jìn)行了沖擊試驗(yàn)。通過統(tǒng)計沖擊斷面上纖維根數(shù),對纖維分散系數(shù)進(jìn)行了計算和擬合;基于威布爾分布,對沖擊試驗(yàn)結(jié)果進(jìn)行了統(tǒng)計分析,建立了不同失效概率下沖擊次數(shù)與纖維摻量間的關(guān)系。結(jié)果表明:摻入鋼纖維可以顯著提高混凝土抗沖擊性能;纖維分散系數(shù)隨摻量的增大呈上升趨勢,雙參數(shù)的威布爾分布可以較好地對沖擊性能進(jìn)行統(tǒng)計分析。
[Abstract]:The volume content of 5 groups of steel fibers was 0 0. 5% and 0. 8%, respectively, by using a drop hammer impact test device, and the volume content of 5 groups of steel fibers was 1.0%. The impact test was carried out on 1.2% steel fiber reinforced concrete round cake specimens. The fiber dispersion coefficient was calculated and fitted by counting the number of fiber roots on the impact section. Based on Weibull distribution, the impact test results are statistically analyzed. The relationship between the number of impact and fiber content under different failure probability is established. The results show that the impact resistance of concrete can be improved significantly by adding steel fiber. The fiber dispersion coefficient increases with the increase of the content of fiber, and the Weibull distribution with two parameters can be used to analyze the impact performance.
【作者單位】： 燕山大學(xué)建筑工程與力學(xué)學(xué)院;
【基金】：國家自然科學(xué)基金(51608469,51578477) 河北省研究生創(chuàng)新能力培養(yǎng)資助項(xiàng)目(CXZZSS2017054)
【分類號】：TU528.572
【正文快照】： 1引言鋼纖維混凝土(Steel Fiber Reinforced Concrete,簡稱SFRC)是在普通混凝土中摻入鋼纖維而得到的新型復(fù)合材料[1]。由于鋼纖維在混凝土基體中隨機(jī)亂向分布,故摻加鋼纖維是提高水泥基復(fù)合材料抗拉強(qiáng)度、抗折強(qiáng)度的最有效方法之一�；炷粱w在承受沖擊荷載作用下開裂,鋼纖