本文關鍵詞：骨料裹漿厚度對混凝土流變性能的影響　出處：《硅酸鹽學報》2017年09期 　論文類型：期刊論文

  更多相關文章： Bingham模型 骨料裹漿厚度 流變性能 組成設計 混凝土

【摘要】：基于Bingham模型,測試了不同骨料裹漿厚度時新拌混凝土的流變參數(shù),探究了骨料裹漿厚度對新拌混凝土流變性能的影響。結果表明,改變骨料裹漿厚度能夠明顯影響新拌混凝土的流變性能。在保持骨料基本參數(shù)不變時,隨著骨料裹漿厚度的增加,混凝土的屈服應力、塑性黏度和靜態(tài)屈服應力基本呈降低趨勢,坍落度逐漸升高,混凝土的流動性得到改善;當在特定水灰比、骨料裹漿厚度相對較高時,拌合物的坍落度較高,且存在輕微離析現(xiàn)象。通過建立流變參數(shù)隨骨料裹漿厚度的變化曲線,能夠確定混凝土中的最佳膠凝材料用量,進而指導混凝土的組成設計。
[Abstract]:Based on the Bingham model, the rheological parameters of fresh concrete with different aggregate thickness were tested, and the effect of aggregate slurry thickness on the rheological properties of fresh concrete was investigated. The rheological properties of fresh concrete can be obviously affected by changing the thickness of aggregate slurry. When the basic parameters of aggregate are kept constant, the yield stress of concrete increases with the increase of aggregate thickness. The plastic viscosity and static yield stress showed a decreasing trend, and the slump gradually increased, and the fluidity of concrete was improved. When the slurry thickness of aggregate is relatively high at the specific water-cement ratio, the slump of the mixture is higher and there is a slight segregation phenomenon. Can determine the optimum amount of cement material in concrete, and then guide the composition design of concrete.
【作者單位】： 湖南大學土木工程學院;中國建筑材料科學研究總院綠色建筑材料國家重點實驗室;廈門理工學院土木工程與建筑系;
【基金】：國家國際科技合作專項(2015DFA50880) 國家自然科學基金(U1305243,51502279)
【分類號】：TU528
【正文快照】： 2.中國建筑材料科學研究總院綠色建筑材料國家重點實驗室,北京100024;3.廈門理工學院土木工程與建筑系,福建廈門361024)根據(jù)富余漿體理論[1],新拌混凝土可看作是粗細骨料分散于漿體相中的多相分散流體,粗骨料之間的空隙由細骨料填充,細骨料之間的空隙則由水泥漿體填充。新拌混

【相似文獻】

相關期刊論文 前10條

1 劉景生;;功能混凝土[J];廣東建材;2007年04期

2 程e，

本文編號：1394661