本文關鍵詞：不同強度等級的高品質(zhì)再生細骨料混凝土試驗研究　出處：《混凝土》2017年11期 　論文類型：期刊論文

  更多相關文章： 再生細骨料混凝土 取代率 強度等級 用水量 抗壓強度 抗氯離子滲透

【摘要】：為擴大再生細骨料的工程使用規(guī)模,采用高品質(zhì)再生細骨料制備再生混凝土,重點研究強度等級和再生細骨料取代率對高品質(zhì)再生細骨料混凝土性能的影響。結果表明:隨著強度等級的增加,高品質(zhì)再生細骨料混凝土的抗壓強度和抗氯離子滲透性能均逐漸增強,而用水量呈現(xiàn)出先減小后增大的趨勢;隨著再生細骨料取代率的增大,其用水量增多,抗壓強度和抗氯離子滲透性能均逐漸降低;當再生細骨料的取代率為100%時,用水量最大增幅為8.0%,28 d抗壓強度最大降幅為9.6%,氯離子擴散系數(shù)最大增加了0.52×10~(-12)m~2/s。
[Abstract]:The influence of strength grade and the substitution rate of recycled fine aggregate on the properties of high quality recycled fine aggregate concrete is studied by using high quality recycled fine aggregate . The results show that with the increase of the strength grade , the compressive strength and the anti - chloride ion permeability of high quality recycled fine aggregate concrete are gradually increased . As the substitution rate of recycled fine aggregate is 100 % , the maximum water consumption is 8.0 % , the maximum compressive strength of 28 d compressive strength is 9.6 % , and the chloride ion diffusion coefficient is increased by 0.52 脳 10 ~ ( -12 ) m ~ 2 / s .

【作者單位】： 遼寧建筑職業(yè)學院;中建三局集團有限公司東北分公司;
【基金】：住房城鄉(xiāng)建設部2016年科學技術項目計劃(2016-R3-003) 遼寧省自然科學基金資助項目(201202097) 遼寧省教育廳科技計劃項目(L2014584)
【分類號】：TU528
【正文快照】： 圖1高品質(zhì)再生細骨料的制備0引言近年來,建筑業(yè)的蓬勃發(fā)展給我們帶來了一系列不可避免的問題:環(huán)境破壞現(xiàn)象嚴重、生態(tài)資源消耗過度、建筑垃圾占用大量耕地等[1-2]。面對這些問題的出現(xiàn),世界各國專家和學者都在加強對建筑垃圾循環(huán)再利用的研究。然而,相比較天然骨料品質(zhì)的穩(wěn)定

【相似文獻】

相關期刊論文 前5條

1 劉炯f，

本文編號：1378162